PBT TV4 261 DSM Additive Manufacturing

So sánh

Bảng thông số kỹ thuật

impact performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Charpy Notched Impact Strength	Charpy Notched Impact Strength -30°C	ISO 179/1eA	9.5 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch 23°C	ISO 179/1eU	68 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch -30°C	ISO 179/1eU	60 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength 23°C	ISO 179/1eA	9.5 kJ/m²

flammability	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Extreme Oxygen Index	Extreme Oxygen Index	ISO 4589-2	20 %
UL flame retardant rating	UL flame retardant rating 1.5mm	IEC 60695-11-10,-20	HB
UL flame retardant rating	UL flame retardant rating 0.71mm	IEC 60695-11-10,-20	HB

flammability

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Extreme Oxygen Index

ISO 4589-2

20 %

UL flame retardant rating

1.5mm

IEC 60695-11-10,-20

UL flame retardant rating

0.71mm

IEC 60695-11-10,-20

mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Tensile modulus	Tensile modulus	ISO 527-2	9750 MPa
tensile strength	tensile strength Break	ISO 527-2	145 MPa
Tensile strain	Tensile strain Break	ISO 527-2	2.8 %

mechanical properties

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Tensile modulus

ISO 527-2

9750 MPa

tensile strength

Break

ISO 527-2

145 MPa

Tensile strain

Break

ISO 527-2

2.8 %

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion TD	ISO 11359-2	7E-05 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion MD	ISO 11359-2	3.5E-05 cm/cm/°C
Melting temperature	Melting temperature	ISO 11357-3	225 °C
Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed	ISO 75-2/A	205 °C
Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 0.45MPa,Unannealed	ISO 75-2/B	220 °C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Water absorption rate	Water absorption rate Equilibrium,23°C,50%RH	ISO 62	0.15 %
Water absorption rate	Water absorption rate	Water absorption rate Saturation,23°C	ISO 62	0.30 %
Shrinkage rate	Shrinkage rate MD	ISO 294-4	0.33 %
Shrinkage rate	Shrinkage rate	Shrinkage rate TD	ISO 294-4	1.2 %
Melt Volume Flow Rate (MVR)	Melt Volume Flow Rate (MVR) 250°C/2.16kg	ISO 1133	18.0 cm³/10min
density	density	ISO 1183	1.51 g/cm³

Electrical performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Compared to the anti leakage trace index	Compared to the anti leakage trace index	IEC 60112	PLC 1
Dissipation factor	Dissipation factor 1MHz	IEC 60250	0.017
Dissipation factor	Dissipation factor	Dissipation factor 100Hz	IEC 60250	2.5E-03
Relative permittivity	Relative permittivity 1MHz	IEC 60250	3.70
Relative permittivity	Relative permittivity	Relative permittivity 100Hz	IEC 60250	3.90
Dielectric strength	Dielectric strength	IEC 60243-1	30 kV/mm
Volume resistivity	Volume resistivity	IEC 60093	>1.0E+15 ohms·cm

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.