| Impact strength of cantilever beam gap | Impact strength of cantilever beam gap | ASTM D256A | 无断裂 |
| Friction coefficient | Friction coefficient Steel - Static | Internal Method | 0.12 |
| compressive strength | compressive strength 10%Strain,23°C | ASTM D695 | 21.4 MPa |
| Compressive modulus | Compressive modulus | ASTM D695 | 536 MPa |
| bending strength | bending strength Yield | ASTM D790 | 22.1 MPa |
| Hot deformation temperature | Hot deformation temperature 1.8MPa,Unannealed | ASTM D648 | 46.7 °C |
| Bending modulus | Bending modulus | ASTM D790 | 758 MPa |
| elongation | elongation Break | ASTM D638 | 200 % |
| tensile strength | tensile strength Ultimate | ASTM D638 | 35.9 MPa |
| limiting pv value | limiting pv value | Internal Method | 0.0701 MPa·m/s |
| UL flame retardant rating | UL flame retardant rating 3.2mm | UL 94 | HB |
| Surface resistivity | Surface resistivity | ASTM D257 | 1.0E+7到1.0E+10 ohms |
| Linear coefficient of thermal expansion | Linear coefficient of thermal expansion MD2：-40to149°C | ASTME831 | 3.4E-04 cm/cm/°C |
| Crystallization peak temperature | Crystallization peak temperature DSC | ASTM D3418 | 135 °C |
| Maximum operating temperature LongTerm, Air | Maximum operating temperature LongTerm, Air | | 82 °C |
| Tensile modulus | Tensile modulus | ASTM D638 | 745 MPa |
| Shore hardness | Shore hardness ShoreD | ASTM D2240 | 66 |
| Water absorption rate | Water absorption rate Saturation | ASTM D570 | <0.010 % |
| Water absorption rate | Water absorption rate 24hr | ASTM D570 | <0.010 % |
| density | density | ASTM D792 | 0.940 g/cm³ |