NBR NANCAR® 1053X26 Nantex Industry Co., Ltd.

So sánh

Bảng thông số kỹ thuật

elastomer	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
tensile strength	tensile strength Yield2	ASTM D412	22.8 MPa
	tensile strength	tensile strength Yield3	ASTM D412	23.2 MPa
	tensile strength	tensile strength	tensile strength Yield4	ASTM D412	23.9 MPa
elongation	elongation Break5	ASTM D412	560 %
	elongation	elongation Break6	ASTM D412	540 %
	elongation	elongation	elongation Break7	ASTM D412	530 %
tear strength	tear strength	ASTM D624	52.0 kN/m
Permanent compression deformation	Permanent compression deformation 100°C,70hr	ASTM D395	49 %
tensile strength	tensile strength 300%Strain5	ASTM D412	9.02 MPa
	tensile strength	tensile strength 300%Strain6	ASTM D412	10.2 MPa
	tensile strength	tensile strength	tensile strength 300%Strain7	ASTM D412	10.5 MPa

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Heat loss	Heat loss	ASTM D5688	0.40 %

thermal performance

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Heat loss

ASTM D5688

0.40 %

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
density	density		0.960 g/cm³
Mooney viscosity	Mooney viscosity ML1+4,100°C	ASTM D1646	52 MU
bound acrylonitrile content	bound acrylonitrile content	Internal Method	26.0 %
stabilizer	stabilizer		Non-staining

hardness	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Shore hardness	Shore hardness ShoreA2	ASTM D2240	66
Shore hardness	Shore hardness ShoreA3	ASTM D2240	67
Shore hardness	Shore hardness ShoreA4	ASTM D2240	68

hardness

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Shore hardness

ShoreA2

ASTM D2240

Shore hardness

ShoreA3

ASTM D2240

Shore hardness

ShoreA4

ASTM D2240

aging	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Volume change	Volume change 100°C,70hr,ASTM标准油（3号）	ASTM D471	38 %
Change rate of hardness (Shore) in the air	Change rate of hardness (Shore) in the air ShoreA,100°C,70hr	ASTM D865	4.0
Change rate of tensile strength in air	Change rate of tensile strength in air 100°C,70hr,在ASTM#1油中	ASTM D471	-9.0 %
Change rate of tensile strength in air	Change rate of tensile strength in air	Change rate of tensile strength in air 100°C,70hr,在ASTM#3油中	ASTM D471	-30 %
Change rate of ultimate elongation in air	Change rate of ultimate elongation in air 100°C,70hr,在ASTM#1油中	ASTM D471	-21 %
Change rate of ultimate elongation in air	Change rate of ultimate elongation in air	Change rate of ultimate elongation in air 100°C,70hr,在ASTM#3油中	ASTM D471	-16 %
Change rate of hardness (Shore) in the air	Change rate of hardness (Shore) in the air 支撐A,100°C,70hr,在ASTM#1油中	ASTM D471	0.0
Change rate of hardness (Shore) in the air	Change rate of hardness (Shore) in the air	Change rate of hardness (Shore) in the air 支撐A,100°C,70hr,在ASTM#3油中	ASTM D471	-18
Volume change	Volume change 100°C,70hr,ASTM标准油（1号）	ASTM D471	2.9 %
Change rate of tensile strength in air	Change rate of tensile strength in air 100°C,70hr	ASTM D865	-1.0 %
Change rate of ultimate elongation in air	Change rate of ultimate elongation in air 100°C,70hr	ASTM D865	-25 %

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.