impact performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength 23°C	ISO 180	无断裂
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C	ISO 180/A	8.0 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch 23°C	ISO 179	无断裂
Charpy Notched Impact Strength	Charpy Notched Impact Strength 23°C	ISO 179/1eA	6.0 kJ/m²

mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Compressive stress	Compressive stress 120°C	ISO 604	65.0 MPa
Compressive stress	Compressive stress	Compressive stress 23°C	ISO 604	105 MPa
bending strength	bending strength 275°C	ISO 178	13.0 MPa
	bending strength	bending strength 175°C	ISO 178	18.0 MPa
		bending strength	bending strength 125°C	ISO 178	70.0 MPa
			bending strength	bending strength 3.5%Strain,23°C	ISO 178	100 MPa
			bending strength	bending strength	bending strength 23°C6	ISO 178	125 MPa
Bending modulus	Bending modulus 23°C	ISO 178	3200 MPa
Tensile strain	Tensile strain Break,23°C	ISO 527-2	25 %
tensile strength	tensile strength Yield,23°C	ISO 527-2	78.0 MPa
Tensile modulus	Tensile modulus 23°C	ISO 527-2	3200 MPa

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Glass transition temperature	Glass transition temperature --8	ISO 11357-2	150 °C
Melting temperature	Melting temperature	ISO 11357-3	343 °C
Glass transition temperature	Glass transition temperature --7	ISO 11357-2	143 °C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion MD:>143°C	ISO 11359-2	1.2E-04 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion TD:<143°C	ISO 11359-2	6E-05 cm/cm/°C
Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed	ISO 75-2/Af	150 °C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion TD:>143°C	ISO 11359-2	1.4E-04 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion MD:<143°C	ISO 11359-2	4E-05 cm/cm/°C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
density	density	ISO 1183	1.40 g/cm³
Spiral flow length	Spiral flow length	Internal Method	13.0 cm
Shrinkage rate	Shrinkage rate TD	ISO 294-4	1.7 %
Shrinkage rate	Shrinkage rate	Shrinkage rate MD	ISO 294-4	1.2 %

Electrical performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Compared to the anti leakage trace index	Compared to the anti leakage trace index	IEC 60112	PLC 4
Dissipation factor	Dissipation factor 23°C,1MHz	IEC 60250	4E-03
Dielectric constant	Dielectric constant 23°C,1kHz	IEC 60250	2.80
Dielectric strength	Dielectric strength 2.00mm	IEC 60243-1	26 kV/mm
Volume resistivity	Volume resistivity 23°C	IEC 60093	1E+16 ohms·cm

hardness	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Shore hardness	Shore hardness ShoreD,23°C	ISO 868	81

hardness

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Shore hardness

ShoreD,23°C

ISO 868

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.