| consumption | consumption 50.8 μm | ASTM D4321 | 39.3 m²/kg |
| Heat sealing strength | Heat sealing strength MD : 177℃ | Internal Method | 890 N/m |
| Water vapor permeability | Water vapor permeability 38℃, 51 μm, 90% RH | ASTM F1249 | 0.14 g/m²/24 hr |
| Oxygen permeability | Oxygen permeability 23℃, 51 μm, 50% RH | ASTM D3985 | 0.33 g/m²/24 hr |
| elongation | elongation MD : Break, 51 μm | ASTM D882 | 400 % |
| tensile strength | tensile strength MD : Break, 51 μm | ASTM D882 | 26.2 MPa |
| film thickness | film thickness | | 1.0 mil |
| film thickness | film thickness 经测试 | ASTM D374 | 25 µm |
| Heat sealing strength | Heat sealing strength 177°C,25.4μm | Internal Method | 890 g/2.5cm |
| Water vapor permeability | Water vapor permeability 25μm,38°C,90%RH | ASTMF1249 | 0.14 g·mm/m²/atm/24hr |
| Usage - Calculated | Usage - Calculated 25.4μm | Internal Method | 39.3 m²/kg |
| Oxygen permeability | Oxygen permeability 23°C,25μm,50%RH | ASTM D3985 | 0.33 cm³·mm/m²/atm/24hr |
| elongation | elongation TD:Break,25μm | ASTM D882 | 550 % |
| elongation | elongation MD:Break,25μm | ASTM D882 | 400 % |
| tensile strength | tensile strength TD:Break,25μm | ASTM D882 | 18.6 MPa |
| tensile strength | tensile strength MD:Break,25μm | ASTM D882 | 26.2 MPa |
| film thickness | film thickness | | 1.0mil(25µ |
| film thickness | film thickness | | 25 µm |