PET TechnoPet GF 20 2 0 TECHNOCOMPOUND GERMANY

So sánh

Bảng thông số kỹ thuật

impact performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch -30°C	ISO 179/1eU	25 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength 23°C	ISO 179/1eA	8.0 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	Charpy Notched Impact Strength -30°C	ISO 179/1eA	8.0 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch 23°C	ISO 179/1eU	25 kJ/m²

flammability	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Burning wire flammability index	Burning wire flammability index 2.0mm	IEC 60695-2-12	750 °C
UL flame retardant rating	UL flame retardant rating 0.8mm	UL 94	HB

flammability

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Burning wire flammability index

2.0mm

IEC 60695-2-12

750 °C

UL flame retardant rating

0.8mm

UL 94

mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Tensile strain	Tensile strain Break	ISO 527-2/5	2.0 %
tensile strength	tensile strength Break	ISO 527-2/5	130 MPa
Tensile modulus	Tensile modulus	ISO 527-2/1	8000 MPa

mechanical properties

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Tensile strain

Break

ISO 527-2/5

2.0 %

tensile strength

Break

ISO 527-2/5

130 MPa

Tensile modulus

ISO 527-2/1

8000 MPa

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Melting temperature	Melting temperature	ISO 11357-3	240 °C
Vicat softening temperature	Vicat softening temperature	ISO 306/B50	250 °C
Hot deformation temperature	Hot deformation temperature 8.0MPa,Unannealed	ISO 75-2/C	75.0 °C
Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed	ISO 75-2/A	215 °C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion MD：23to80°C	ISO 11359-2	3E-05 cm/cm/°C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Viscosity value	Viscosity value 降低的粘度	ISO 1628	66.0 ml/g
Water absorption rate	Water absorption rate Saturation,23°C	ISO 62	0.45 %
Water absorption rate	Water absorption rate	Water absorption rate 23°C,24hr	ISO 62	0.20 %
Shrinkage rate	Shrinkage rate MD	ISO 2577	0.30 %
Shrinkage rate	Shrinkage rate	Shrinkage rate TD	ISO 2577	1.1 %
density	density	ISO 1183	1.51 g/cm³

Electrical performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Compared to the anti leakage trace index	Compared to the anti leakage trace index SolutionA	IEC 60112	PLC 2
Relative permittivity	Relative permittivity 1MHz	IEC 60250	4.10
Relative permittivity	Relative permittivity	Relative permittivity 100Hz	IEC 60250	4.60
Dielectric strength	Dielectric strength 1.00mm	IEC 60243-1	31 kV/mm
Volume resistivity	Volume resistivity	IEC 60093	>1.0E+16 ohms·cm
Surface resistivity	Surface resistivity	IEC 60093	>1.0E+14 ohms

hardness	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Ball Pressure Test	Ball Pressure Test	ISO 2039-1	230 MPa

hardness

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Ball Pressure Test

ISO 2039-1

230 MPa

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.