| Shore hardness | Shore hardness ShoreD | ASTM D2240 | 67 |
| Impact strength of cantilever beam gap | Impact strength of cantilever beam gap 23°C | ASTM D256 | NoBreak |
| compressive strength | compressive strength 23°C | ASTM D695 | 17.0 MPa |
| Bending modulus | Bending modulus 23°C | ASTM D790 | 1000 MPa |
| elongation | elongation Break,23°C | ASTM D638 | 300 % |
| tensile strength | tensile strength 23°C | ASTM D638 | 40.0 MPa |
| Water absorption rate | Water absorption rate 24hr | ASTM D570 | 7E-03 % |
| melt mass-flow rate | melt mass-flow rate 297°C/5.0kg | ASTM D3159 | 6.0 g/10min |
| Apparent density | Apparent density | Internal Method | 1.30 g/cm³ |
| density | density | ASTM D792 | 1.70 g/cm³ |
| Extreme Oxygen Index | Extreme Oxygen Index | ASTM D2863 | 30to32 % |
| UL flame retardant rating | UL flame retardant rating | UL 94 | V-0 |
| Arc resistance | Arc resistance | ASTM D495 | 122 sec |
| Dissipation factor | Dissipation factor 23°C,1MHz | ASTM D1531 | 6E-03 |
| Dielectric constant | Dielectric constant 23°C,1MHz | ASTM D1531 | 2.50to2.60 |
| Dielectric strength | Dielectric strength 0.250mm | ASTM D149 | 70 kV/mm |
| Volume resistivity | Volume resistivity | ASTM D257 | 1E+17 ohms·cm |
| Maximum operating temperature | Maximum operating temperature | UL 746 | 155 °C |
| Linear coefficient of thermal expansion | Linear coefficient of thermal expansion MD：0to100°C | ASTM D696 | 1.3E-04 cm/cm/°C |
| Melting temperature | Melting temperature | ASTM D3418 | 255to280 °C |