| density | density | ISO 1183 | 1.16 g/cm³ |
| UL flame retardant rating | UL flame retardant rating 3.2mm | UL 94 | HB |
| Linear coefficient of thermal expansion | Linear coefficient of thermal expansion TD | ASTME831 | 1.3E-04 cm/cm/°C |
| Linear coefficient of thermal expansion | Linear coefficient of thermal expansion MD:-30to100°C | ASTME831 | 4.5E-05 cm/cm/°C |
| Hot deformation temperature | Hot deformation temperature 1.8MPa,Unannealed | ISO 75-2/A | 60.2 °C |
| Hot deformation temperature | Hot deformation temperature 0.45MPa,Unannealed | ISO 75-2/Bf | 114 °C |
| Dart impact | Dart impact -30°C,TotalEnergy,韧性破坏 | ASTM D3763 | 48.6 J |
| Impact strength of cantilever beam gap | Impact strength of cantilever beam gap 23°C | ISO 180 | 54 kJ/m² |
| Impact strength of cantilever beam gap | Impact strength of cantilever beam gap -30°C | ISO 180 | 4.7 kJ/m² |
| Tensile strain | Tensile strain Break,233°C | ISO 527-2 | >200 % |
| tensile strength | tensile strength Yield,23°C3 | ISO 527-2 | 23.6 MPa |
| tensile strength | tensile strength Yield | ASTM D638 | 22.9 MPa |
| Shrinkage rate | Shrinkage rate 23°C,24hr,3.18mm | ISO 294-4 | 0.70to0.90 % |
| melt mass-flow rate | melt mass-flow rate 230°C/2.16kg | ISO 1133 | 0.50 g/10min |
| gloss | gloss 60°,3180μm,热塑,光滑 | ISO 2813 | 20to40 |
| Impact strength of cantilever beam gap | Impact strength of cantilever beam gap -30°C | ASTM D256 | 53 J/m |
| Charpy Notched Impact Strength | Charpy Notched Impact Strength 23°C | ISO 179 | 62 kJ/m² |
| Charpy Notched Impact Strength | Charpy Notched Impact Strength -30°C | ISO 179 | 4.1 kJ/m² |
| Bending modulus | Bending modulus 23°C | ISO 178 | 2510 MPa |
| Impact strength of cantilever beam gap | Impact strength of cantilever beam gap 23°C | ASTM D256 | 860 J/m |