PP TU 76 V Ducor Petrochemicals BV

So sánh

Bảng thông số kỹ thuật

impact performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C,Partial Break	ISO 180/1A	18 kJ/m²
	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 0°C	ISO 180/1A	9.0 kJ/m²
		Impact strength of cantilever beam gap	Impact strength of cantilever beam gap -20°C	ISO 180/1A	5.5 kJ/m²
		Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap -30°C	ISO 180/1A	4.5 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch 23°C	ISO 179/1eU	无断裂
	Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch 0°C	ISO 179/1eU	无断裂
		Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch -20°C	ISO 179/1eU	150 kJ/m²
		Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch -30°C	ISO 179/1eU	130 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength 23°C,Partial Break	ISO 179/1eA	20 kJ/m²
	Charpy Notched Impact Strength	Charpy Notched Impact Strength 0°C	ISO 179/1eA	9.0 kJ/m²
		Charpy Notched Impact Strength	Charpy Notched Impact Strength -20°C	ISO 179/1eA	4.5 kJ/m²
		Charpy Notched Impact Strength	Charpy Notched Impact Strength	Charpy Notched Impact Strength -30°C	ISO 179/1eA	4.0 kJ/m²

mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
shear modulus	shear modulus	ISO 6721-2	500 MPa
Tensile strain	Tensile strain Break	ISO 527-2/50	>50 %
Tensile strain	Tensile strain	Tensile strain Yield	ISO 527-2/50	5.0 %
tensile strength	tensile strength Yield	ISO 527-2/50	19.0 MPa
Tensile modulus	Tensile modulus	ISO 527-2/1	950 MPa

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed	ISO 75-2/A	48.0 °C
Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 0.45MPa,Unannealed	ISO 75-2/B	78.0 °C
Melting temperature	Melting temperature	ISO 3146	163 °C
Vicat softening temperature	Vicat softening temperature --	ISO 306/B	56.0 °C
Vicat softening temperature	Vicat softening temperature	Vicat softening temperature --	ISO 306/A	142 °C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
melt mass-flow rate	melt mass-flow rate 230°C/2.16kg	ISO 1133	48 g/10min
density	density	ISO 1183	0.910 g/cm³

Physical properties

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

melt mass-flow rate

230°C/2.16kg

ISO 1133

48 g/10min

density

ISO 1183

0.910 g/cm³

hardness	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Ball Pressure Test	Ball Pressure Test H132/30	ISO 2039-1	44.0 MPa

hardness

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Ball Pressure Test

H132/30

ISO 2039-1

44.0 MPa

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.