| impact performance | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| Dart impact | Dart impact 23°C,TotalEnergy | ASTM D3763 | 50.0 J |
| Suspended wall beam without notch impact strength | Suspended wall beam without notch impact strength 23°C | ISO 180/1U | NoBreak |
| Impact strength of simply supported beam without notch | Impact strength of simply supported beam without notch 23°C | ISO 179/1eU | NoBreak |
| Impact strength of cantilever beam gap | Impact strength of cantilever beam gap -30°C | ISO 180/1A | 50 kJ/m² |
| Impact strength of cantilever beam gap | Impact strength of cantilever beam gap 23°C | ISO 180/1A | 70 kJ/m² |
| Suspended wall beam without notch impact strength | Suspended wall beam without notch impact strength -30°C | ISO 180/1U | NoBreak |
| Charpy Notched Impact Strength | Charpy Notched Impact Strength -30°C | ISO 179/1eA | 60 kJ/m² |
| Charpy Notched Impact Strength | Charpy Notched Impact Strength 23°C | ISO 179/1eA | 75 kJ/m² |
| Impact strength of simply supported beam without notch | Impact strength of simply supported beam without notch -30°C | ISO 179/1eU | NoBreak |
| flammability | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| UL flame retardant rating | UL flame retardant rating 1.5mm | UL 94 | V-0 |
| UL flame retardant rating | UL flame retardant rating 3.0mm | UL 94 | 5VA |
| Burning wire flammability index | Burning wire flammability index 1.0mm | IEC 60695-2-12 | 960 °C |
| Hot filament ignition temperature | Hot filament ignition temperature 1.0mm | IEC 60695-2-13 | 825 °C |
| mechanical properties | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| Tensile modulus | Tensile modulus | ASTM D638 | 2100 Mpa |
| Tensile modulus | Tensile modulus | ISO 527-2/1 | 2100 Mpa |
| bending strength | bending strength | ISO 178 | 85.0 Mpa |
| Bending modulus | Bending modulus | ISO 178 | 2200 Mpa |
| Bending modulus | Bending modulus 50.0mmSpan | ASTM D790 | 2060 Mpa |
| Tensile strain | Tensile strain Break | ISO 527-2/50 | 130 % |
| elongation | elongation Break | ASTM D638 | 130 % |
| Tensile strain | Tensile strain Yield | ISO 527-2/50 | 6.0 % |
| elongation | elongation Yield | ASTM D638 | 6.0 % |
| tensile strength | tensile strength Break | ISO 527-2/50 | 60.0 Mpa |
| tensile strength | tensile strength Break | ASTM D638 | 60.0 Mpa |
| tensile strength | tensile strength Yield | ISO 527-2/50 | 55.0 Mpa |
| tensile strength | tensile strength Yield | ASTM D638 | 58.0 Mpa |
| bending strength | bending strength Yield,50.0mmSpan | ASTM D790 | 89.0 Mpa |
| thermal performance | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| Linear coefficient of thermal expansion | Linear coefficient of thermal expansion TD：-40to40°C | ASTME831 | 6.5E-05 cm/cm/°C |
| Linear coefficient of thermal expansion | Linear coefficient of thermal expansion MD：23to80°C | ISO 11359-2 | 7.2E-05 cm/cm/°C |
| Linear coefficient of thermal expansion | Linear coefficient of thermal expansion MD：-40to40°C | ASTME831 | 6.5E-05 cm/cm/°C |
| Ball Pressure Test | Ball Pressure Test 125°C | IEC 60695-10-2 | Pass |
| Vicat softening temperature | Vicat softening temperature | ISO 306/B120 | 140 °C |
| Vicat softening temperature | Vicat softening temperature | ASTM D15259 | 140 °C |
| Hot deformation temperature | Hot deformation temperature 1.8MPa,Unannealed,3.20mm | ASTM D648 | 120 °C |
| Hot deformation temperature | Hot deformation temperature 0.45MPa,Unannealed,3.20mm | ASTM D648 | 135 °C |
| Linear coefficient of thermal expansion | Linear coefficient of thermal expansion TD：23to80°C | ISO 11359-2 | 7.7E-05 cm/cm/°C |
| RTI Elec | RTI Elec | UL 746 | 125 °C |
| RTI Imp | RTI Imp | UL 746 | 115 °C |
| RTI Str | RTI Str | UL 746 | 120 °C |
| Physical properties | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| Water absorption rate | Water absorption rate Saturation,23°C | ISO 62 | 0.35 % |
| Water absorption rate | Water absorption rate Equilibrium,23°C,50%RH | ISO 62 | 0.15 % |
| Shrinkage rate | Shrinkage rate TD：3.20mm | Internal Method | 0.40-0.80 % |
| Shrinkage rate | Shrinkage rate MD：3.20mm | Internal Method | 0.40-0.80 % |
| Melt Volume Flow Rate (MVR) | Melt Volume Flow Rate (MVR) 300°C/1.2kg | ISO 1133 | 9.00 cm3/10min |
| melt mass-flow rate | melt mass-flow rate 300°C/1.2kg | ASTM D1238 | 10 g/10min |
| Electrical performance | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| Dielectric strength | Dielectric strength 3.20mm,inOil | ASTM D149 | 17 KV/mm |
| Dielectric strength | Dielectric strength 3.20mm,in Oil | IEC 60243-1 | 16 KV/mm |
| Dielectric constant | Dielectric constant 50Hz | ASTM D150 | 2.95 |
| Dielectric constant | Dielectric constant 60Hz | ASTM D150 | 2.95 |
| Dielectric constant | Dielectric constant 1MHz | ASTM D150 | 2.90 |
| Dissipation factor | Dissipation factor 50Hz | ASTM D150 | 2.4E-03 |
| Dissipation factor | Dissipation factor 60Hz | ASTM D150 | 2.4E-03 |
| Dissipation factor | Dissipation factor 1MHz | ASTM D150 | 8.5E-03 |
| Compared to the anti leakage trace index | Compared to the anti leakage trace index CTI | UL 746 | PLC 3 |
| Compared to the anti leakage trace index | Compared to the anti leakage trace index | IEC 60112 | V |
| High arc combustion index | High arc combustion index HAI | UL 746 | PLC 0 |
| Hot wire ignition | Hot wire ignition HWI | UL 746 | PLC 1 |