mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Rockwell hardness	Rockwell hardness	ISO 2039	R108
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap -30℃,6.4mm	ASTM D-256	70 J/m
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23℃,6.4mm	ASTM D-256	150 J/m
Charpy Notched Impact Strength	Charpy Notched Impact Strength -30℃	ISO 179/1eA	7 KJ/m
Charpy Notched Impact Strength	Charpy Notched Impact Strength	Charpy Notched Impact Strength 23℃	ISO 179/1eA	15 KJ/m
Bending modulus	Bending modulus	ISO 178	1900 Mpa
bending strength	bending strength	ISO 178	65 Mpa
tensile strength	tensile strength	ISO 527	45 Mpa

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Combustibility	Combustibility	UL 94	HB
Ball indentation temperature	Ball indentation temperature		90 °C
Hot deformation temperature	Hot deformation temperature 1.82MPa,12.7mm	ASTM D-648	86 °C
Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 1.80MPa,12.7mm	ISO 75/A	76 °C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Shrinkage rate	Shrinkage rate	ASTM D-955	0.4-0.6 %

Physical properties

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Shrinkage rate

ASTM D-955

0.4-0.6 %

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.