PA66 LNP™ LUBRICOMP™ RFN16SXZ compound SABIC

So sánh

Bảng thông số kỹ thuật

impact performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C	ASTM D256	80 J/m
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C3	ISO 180/1A	8.0 kJ/m²
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength 23°C	ASTM D4812	870 J/m
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength 23°C3	ISO 180/1U	58 kJ/m²
Dart impact	Dart impact 23°C,EnergyatPeakLoad	ASTM D3763	9.20 J
Dart impact	Dart impact	Dart impact --	ISO 6603-2	2.30 J

mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Bending modulus	Bending modulus --	ASTM D790	8410 MPa
Bending modulus	Bending modulus	Bending modulus --	ISO 178	9800 MPa
bending strength	bending strength --	ASTM D790	247 MPa
Tensile modulus	Tensile modulus --2	ASTM D638	10700 MPa
Tensile modulus	Tensile modulus	Tensile modulus --	ISO 527-2/1	9900 MPa
tensile strength	tensile strength Break	ASTM D638	161 MPa
tensile strength	tensile strength	tensile strength Break	ISO 527-2	163 MPa
elongation	elongation Break	ASTM D638	2.8 %
elongation	elongation	elongation Break	ISO 527-2	3.0 %
bending strength	bending strength --	ISO 178	255 MPa
Friction coefficient	Friction coefficient Dynamic	ASTM D3702Modified	0.43
Friction coefficient	Friction coefficient	Friction coefficient Static	ASTM D3702Modified	0.49
Wear factor	Wear factor Washer	ASTM D3702Modified	159 10^-10in^5-min/ft-lb-hr

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion MD:-40to40°C	ASTME831	3.1E-05 cm/cm/°C
	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion MD:-40to40°C	ISO 11359-2	3.2E-05 cm/cm/°C
	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion TD:-40to40°C	ASTME831	6.3E-05 cm/cm/°C
Hot deformation temperature	Hot deformation temperature 0.45MPa,Unannealed,3.20mm	ASTM D648	261 °C
	Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed,3.20mm	ASTM D648	249 °C
	Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed,64.0mmSpan4	ISO 75-2/Af	220 °C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
density	density	ASTMD792	1.41 g/cm³
Shrinkage rate	Shrinkage rate MD:24hr	ASTM D955	0.30 %
	Shrinkage rate	Shrinkage rate TD:24hr	ASTM D955	1.3 %
		Shrinkage rate	Shrinkage rate TD:24hr	ISO 294-4	1.3 %
		Shrinkage rate	Shrinkage rate	Shrinkage rate MD:24hr	ISO 294-4	0.28 %
Water absorption rate	Water absorption rate 24hr,50%RH	ASTM D570	0.65 %
Water absorption rate	Water absorption rate	Water absorption rate Equilibrium,23°C,50%RH	ISO 62	1.1 %

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.