PA612/F/PTFE LNP™ LUBRICOMP™ IFL-4036 SABIC INNOVATIVE US

246

Đặc tính:
Chống mài mòn
Lĩnh vực ứng dụng:
Phụ kiện điện tử
So sánh
Xem giá

Bảng thông số kỹ thuật

impact performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Multi axis Instrumented Impact Energy	Multi axis Instrumented Impact Energy	ISO 6603-2	4.27 J
Dart impact	Dart impact 23°C,EnergyatPeakLoad	ASTM D3763	17.7 J
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength 23°C	ISO 180/1U	73 kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C	ISO 180/1A	12 kJ/m²

mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
tensile strength	tensile strength Break	ISO 527-2	157 Mpa
elongation	elongation Break	ASTM D638	3.2 %
Tensile strain	Tensile strain Break	ISO 527-2	3.0 %
tensile strength	tensile strength Break	ASTM D638	154 Mpa
Tensile modulus	Tensile modulus	ISO 527-2/1	10300 Mpa
Tensile modulus	Tensile modulus	Tensile modulus	ASTM D638	9970 Mpa
bending strength	bending strength	ASTM D790	241 Mpa
Bending modulus	Bending modulus	ISO 178	7920 Mpa
Bending modulus	Bending modulus	Bending modulus	ASTM D790	8620 Mpa
Wear factor	Wear factor Washer	ASTM D3702Modified	9.00 10^-10in^5-min/ft-lb-hr
Friction coefficient	Friction coefficient Static	ASTM D3702Modified	0.51
Friction coefficient	Friction coefficient	Friction coefficient Dynamic	ASTM D3702Modified	0.55
bending strength	bending strength	ISO 178	232 Mpa

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion TD：-40to40°C	ASTME831	7.6E-05 cm/cm/°C
	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion TD：-40to40°C	ISO 11359-2	7.7E-05 cm/cm/°C
		Linear coefficient of thermal expansion	Linear coefficient of thermal expansion MD：-40to40°C	ISO 11359-2	2.6E-05 cm/cm/°C
		Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion MD：-40to40°C	ASTME831	2.5E-05 cm/cm/°C
Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed,64.0mmSpan	ISO 75-2/Af	198 °C
Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed,3.20mm	ASTM D648	201 °C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Water absorption rate	Water absorption rate Equilibrium,23°C,50%RH	ISO 62	0.17 %
Water absorption rate	Water absorption rate	Water absorption rate 24hr,50%RH	ASTM D570	0.10 %
Shrinkage rate	Shrinkage rate MD:24hr	ISO 294-4	0.24 %
	Shrinkage rate	Shrinkage rate TD:24hr	ISO 294-4	0.84 %
		Shrinkage rate	Shrinkage rate TD：24hr	ASTM D955	0.80 %
		Shrinkage rate	Shrinkage rate	Shrinkage rate MD：24hr	ASTM D955	0.20 %

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.

Có thể bạn cũng quan tâm

PA612/F/PTFE IFL-4036 Nhựa đổi mới cơ bản (Mỹ)

₫195.410/KG