mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Charpy Notched Impact Strength	Charpy Notched Impact Strength 23℃	ISO 179/1eA	7 KJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap -40℃	ISO 180/1A	5 KJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23℃	ISO 180/1A	6 KJ/m²
bending strength	bending strength 23℃	ISO 178	140 N/mm²
Bending modulus	Bending modulus 23℃	ISO 178	6950 N/mm²
Tensile stress	Tensile stress 23℃，Break	ISO 527-2	3 %
tensile strength	tensile strength 23℃，Break	ISO 527-2	100 N/mm²
Tensile modulus	Tensile modulus 23℃	ISO 527-2	7200 N/mm²
Shore hardness	Shore hardness	ISO 865	83

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Hot deformation temperature	Hot deformation temperature HDT	ISO 75-2/A	160 ℃
Melting temperature	Melting temperature	ISO 3146	212 ℃
Vicat softening temperature	Vicat softening temperature	ISO 306/B50	162 ℃

thermal performance

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Hot deformation temperature

HDT

ISO 75-2/A

160 ℃

Melting temperature

ISO 3146

212 ℃

Vicat softening temperature

ISO 306/B50

162 ℃

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
density	density 23℃	ISO 1183	1.57 g/cm³
Shrinkage rate	Shrinkage rate	ISO 294-4	0.4-0.7 %
water content	water content	ISO 15512	0.2 %
ash content	ash content	ISO 3451-4	25 %

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.