| Burning rate | Burning rate | ISO 3795 | 30 mm/min |
| UL flame retardant rating | UL flame retardant rating 1.5mm | IEC 60695-11-10,-20 | HB |
| UL flame retardant rating | UL flame retardant rating 3.0mm | IEC 60695-11-10,-20 | HB |
| Burning wire flammability index | Burning wire flammability index 1.5mm | IEC 60695-2-12 | 675 °C |
| Burning wire flammability index | Burning wire flammability index 3.0mm | IEC 60695-2-12 | 675 °C |
| Hot filament ignition temperature | Hot filament ignition temperature 1.5mm | IEC 60695-2-13 | 700 °C |
| density | density | ISO 1183/A | 1.18 g/cm³ |
| Melt Volume Flow Rate (MVR) | Melt Volume Flow Rate (MVR) 250°C/5.0kg | ISO 1133 | 6.00 cm³/10min |
| Tensile modulus | Tensile modulus | ISO 527-2/1A/1 | 3100 MPa |
| tensile strength | tensile strength Yield | ISO 527-2/1A/50 | 51.0 MPa |
| Tensile strain | Tensile strain Yield | ISO 527-2/1A/50 | 3.1 % |
| Charpy Notched Impact Strength | Charpy Notched Impact Strength -30°C | ISO 179/1eA | 4.0 kJ/m² |
| Charpy Notched Impact Strength | Charpy Notched Impact Strength 23°C | ISO 179/1eA | 10 kJ/m² |
| Impact strength of simply supported beam without notch | Impact strength of simply supported beam without notch -30°C | ISO 179/1eU | 75 kJ/m² |
| Impact strength of simply supported beam without notch | Impact strength of simply supported beam without notch 23°C | ISO 179/1eU | NoBreak |
| Ball Pressure Test | Ball Pressure Test H358/10 | ISO 2039-1 | 101 MPa |
| Hot deformation temperature | Hot deformation temperature 0.45MPa,Unannealed | ISO 75-2/Bf | 96.0 °C |
| Hot filament ignition temperature | Hot filament ignition temperature 3.0mm | IEC 60695-2-13 | 700 °C |
| Hot deformation temperature | Hot deformation temperature 1.8MPa,Unannealed | ISO 75-2/Af | 78.0 °C |
| Vicat softening temperature | Vicat softening temperature -- | ISO 306/A50 | 184 °C |
| Vicat softening temperature | Vicat softening temperature -- | ISO 306/B50 | 110 °C |