PBT VALOX™ 357-7001 SABIC EU

102

Đặc tính:
Chống cháy
Chống tia cực tím
Lĩnh vực ứng dụng:
Thiết bị điện
Túi nhựa
Trang chủ
Hàng gia dụng
Trang chủ
Nhà ở
Công tắc
Giấy chứng nhận:
UL
So sánh

Bảng thông số kỹ thuật

impact performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Charpy Notched Impact Strength	Charpy Notched Impact Strength 23°C	ISO 179/1eA	45 kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap -30°C	ASTM D256	150 J/m
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C	ASTM D256	320 J/m
Dart impact	Dart impact 23°C	ASTM D3029	43.4 J
Dart impact	Dart impact	Dart impact 23°C11	ASTM D3029	43.0 J
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap -30°C	ISO 180/1A	10 kJ/m²
	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C	ISO 180/1A	45 kJ/m²
	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C	ASTM D4812	NoBreak
Dart impact	Dart impact 23°C,TotalEnergy	ASTM D3763	35.8 J

flammability	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
UL flame retardant rating	UL flame retardant rating 0.46mm	UL 94	HB
	UL flame retardant rating	UL flame retardant rating 0.63mm	UL 94	V-0
	UL flame retardant rating	UL flame retardant rating	UL flame retardant rating 3.0mm	UL 94	5VA
Burning wire flammability index	Burning wire flammability index 1.0mm	IEC 60695-2-12	960 °C
Hot filament ignition temperature	Hot filament ignition temperature 1.0mm	IEC 60695-2-13	775 °C
	Hot filament ignition temperature	Hot filament ignition temperature 2.0mm	IEC 60695-2-13	750 °C
	Hot filament ignition temperature	Hot filament ignition temperature	Hot filament ignition temperature 3.0mm	IEC 60695-2-13	725 °C
Extreme Oxygen Index	Extreme Oxygen Index	ASTM D2863	30 %

mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
bending strength	bending strength Break,50.0mmSpan	ASTM D790	78.0 Mpa
	bending strength	bending strength Yield,50.0mmSpan	ASTM D790	78.0 Mpa
	bending strength	bending strength	bending strength	ISO 178	73.0 Mpa
Bending modulus	Bending modulus	ISO 178	2000 Mpa
Bending modulus	Bending modulus	Bending modulus 50.0mmSpan	ASTM D790	2100 Mpa
Tensile strain	Tensile strain Yield	ISO 527-2/50	5.0 %
Tensile strain	Tensile strain	Tensile strain Yield	ASTM D638	5.0 %
tensile strength	tensile strength Break	ISO 527-2/50	40.0 Mpa
Tensile strain	Tensile strain Break	ISO 527-2/50	30 %
Tensile strain	Tensile strain	Tensile strain Break	ASTM D638	54 %
tensile strength	tensile strength Yield	ISO 527-2/50	50.0 Mpa
tensile strength	tensile strength	tensile strength Break	ASTM D638	42.0 Mpa
Tensile modulus	Tensile modulus	ASTM D638	2020 Mpa
Tensile modulus	Tensile modulus	Tensile modulus	ISO 527-2/1	2200 Mpa
tensile strength	tensile strength Yield	ASTM D638	48.0 Mpa

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
RTI Elec	RTI Elec	UL 746	120 °C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion TD：-40to40°C	ISO 11359-2	8.4E-05 cm/cm/°C
	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion TD：-40to40°C	ASTME831	8.4E-05 cm/cm/°C
		Linear coefficient of thermal expansion	Linear coefficient of thermal expansion MD：-40to40°C	ISO 11359-2	7.2E-05 cm/cm/°C
		Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion MD：60to138°C	ASTME831	1.2E-04 cm/cm/°C
Vicat softening temperature	Vicat softening temperature --	ISO 306/B50	145 °C
Vicat softening temperature	Vicat softening temperature	Vicat softening temperature	ASTM D152513	134 °C
Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed,64.0mmSpan	ISO 75-2/Af	84.0 °C
	Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed,6.40mm	ASTM D648	99.0 °C
		Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed,3.20mm	ASTM D648	98.0 °C
			Hot deformation temperature	Hot deformation temperature 0.45MPa,Unannealed,6.40mm	ASTM D648	138 °C
			Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 0.45MPa,Unannealed,3.20mm	ASTM D648	135 °C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion MD：-40to40°C	ASTME831	9.2E-05 cm/cm/°C
Ball Pressure Test	Ball Pressure Test 125°C	IEC 60695-10-2	Pass
Vicat softening temperature	Vicat softening temperature --	ISO 306/B120	150 °C
RTI Imp	RTI Imp	UL 746	120 °C
RTI Str	RTI Str	UL 746	140 °C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Shrinkage rate	Shrinkage rate TD：--3	Internal Method	1.2-1.6 %
Water absorption rate	Water absorption rate 24hr	ASTM D570	0.080 %
	Water absorption rate	Water absorption rate Saturation,23°C	ISO 62	0.50 %
	Water absorption rate	Water absorption rate	Water absorption rate Equilibrium,23°C,50%RH	ISO 62	0.15 %
Outdoor applicability	Outdoor applicability	UL 746C	f2
density	density	ASTM D792	1.35 g/cm³
Specific volume	Specific volume	ASTM D792	0.740 cm³/g
density	density	ISO 1183	1.34 g/cm³
melt mass-flow rate	melt mass-flow rate 250°C/5.0kg	ASTM D1238	9.6 g/10min
Melt Volume Flow Rate (MVR)	Melt Volume Flow Rate (MVR) 250°C/5.0kg	ISO 1133	8.00 cm3/10min
Shrinkage rate	Shrinkage rate MD：--2	Internal Method	0.80-1.1 %
	Shrinkage rate	Shrinkage rate MD：--3	Internal Method	1.0-1.4 %
		Shrinkage rate	Shrinkage rate MD：3.20mm	Internal Method	1.0-1.4 %
		Shrinkage rate	Shrinkage rate	Shrinkage rate TD：--2	Internal Method	0.90-1.3 %

Electrical performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Volume resistivity	Volume resistivity	ASTM D257	>1.2E+16 ohms·cm
Dielectric strength	Dielectric strength 1.60mm,in Oil	ASTM D149	25 KV/mm
Dielectric strength	Dielectric strength	Dielectric strength 3.20mm,inAir	ASTM D149	19 KV/mm
Dielectric constant	Dielectric constant 1MHz	ASTM D150	3.20
Dissipation factor	Dissipation factor 100Hz	ASTM D150	3E-03
Dielectric strength	Dielectric strength 3.20mm,in Oil	ASTM D149	19 KV/mm
Dielectric constant	Dielectric constant 100Hz	ASTM D150	3.20
Dissipation factor	Dissipation factor 1MHz	ASTM D150	0.030
Arc resistance	Arc resistance	ASTM D495	PLC6
Compared to the anti leakage trace index	Compared to the anti leakage trace index CTI	UL 746	PLC 2
High arc combustion index	High arc combustion index HAI	UL 746	PLC 3
High voltage arc tracing rate	High voltage arc tracing rate HVTR	UL 746	PLC 3
Hot wire ignition	Hot wire ignition HWI	UL 746	PLC 2

hardness	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Rockwell hardness	Rockwell hardness R-Scale	ASTM D785	117

hardness

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Rockwell hardness

R-Scale

ASTM D785

117

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.