impact performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C,3.20mm	ASTM D256	90 J/m
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C	ASTM D256	NoBreak
InstrumentedDartImpact	InstrumentedDartImpact 23°C,3.20mm,TotalEnergy	ASTM D3763	90.0 J

impact performance

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Impact strength of cantilever beam gap

23°C,3.20mm

ASTM D256

90 J/m

Impact strength of cantilever beam gap

23°C

ASTM D256

NoBreak

InstrumentedDartImpact

23°C,3.20mm,TotalEnergy

ASTM D3763

90.0 J

flammability	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Extreme Oxygen Index	Extreme Oxygen Index	ASTM D2863	26 %
Average degree of combustion	Average degree of combustion	ASTM D635	3 cm
UL flame retardant rating	UL flame retardant rating 0.50mm	UL 94	V-2
	UL flame retardant rating	UL flame retardant rating 1.6mm	UL 94	V-2
		UL flame retardant rating	UL flame retardant rating 2.5mm	UL 94	V-2
		UL flame retardant rating	UL flame retardant rating	UL flame retardant rating 3.0mm	UL 94	V-2
Ignition temperature of heating wire	Ignition temperature of heating wire 2.0mm	IEC 60695-2-13	850 °C

mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Tensile modulus	Tensile modulus	ASTM D638	2410 MPa
tensile strength	tensile strength Yield	ASTM D638	60.0 MPa
tensile strength	tensile strength	tensile strength Break	ASTM D638	72.0 MPa
elongation	elongation Yield	ASTM D638	6.0 %
elongation	elongation	elongation Break	ASTM D638	150 %
Bending modulus	Bending modulus	ASTM D790	2410 MPa
bending strength	bending strength	ASTM D790	96.0 MPa
Wear resistance	Wear resistance 雾度变化	ASTM D1004	45 %

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Hot deformation temperature	Hot deformation temperature 0.45MPa,Annealed,4.00mm	ASTM D648	145 °C
	Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed,4.00mm	ASTM D648	129 °C
	Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 1.8MPa,Annealed,4.00mm	ASTM D648	142 °C
Vicat softening temperature	Vicat softening temperature	ASTM D15255	151 °C
Ball pressure temperature	Ball pressure temperature	IEC 60598-1	>125 °C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion MD：-40to82°C	ASTM D696	6.8E-05 cm/cm/°C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
density	density	ASTM D792	1.20 g/cm³
melt mass-flow rate	melt mass-flow rate 300°C/1.2kg	ASTM D1238	7.0 g/10min
Shrinkage rate	Shrinkage rate MD	ASTM D955	0.50to0.70 %
Water absorption rate	Water absorption rate 23°C,24hr	ASTM D570	0.15 %
Water absorption rate	Water absorption rate	Water absorption rate Equilibrium,23°C,50%RH	ASTM D570	0.32 %

Electrical performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Volume resistivity	Volume resistivity 23°C	ASTM D257	2E+17 ohms·cm
Dielectric strength	Dielectric strength	ASTM D149	17 kV/mm
Dielectric constant	Dielectric constant 60Hz	ASTM D150	3.00
Dissipation factor	Dissipation factor 60Hz	ASTM D150	1E-03
Compared to the anti leakage trace index	Compared to the anti leakage trace index 2.00mm	IEC 60112	PLC 2

hardness	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Rockwell hardness	Rockwell hardness M-Sale	ASTM D785	74
Rockwell hardness	Rockwell hardness R-Sale	ASTM D785	118

hardness

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Rockwell hardness

M-Sale

ASTM D785

Rockwell hardness

R-Sale

ASTM D785

118

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.