impact performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch 23°C	ISO 179	190 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch -30°C	ISO 179	100 kJ/m²

impact performance

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Impact strength of simply supported beam without notch

23°C

ISO 179

190 kJ/m²

Impact strength of simply supported beam without notch

-30°C

ISO 179

100 kJ/m²

mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
elongation	elongation Break	ASTM D638	3.0 %
Nominal tensile fracture strain	Nominal tensile fracture strain 23°C	ISO 527-2	9.0 %
Tensile strain	Tensile strain Yield,23°C	ISO 527-2	3.0 %
tensile strength	tensile strength Yield,23°C	ISO 527-2	51.0 Mpa
tensile strength	tensile strength	tensile strength Yield,23°C	ASTM D638	52.0 Mpa
bending strength	bending strength	ISO 178	72.0 Mpa
Tensile modulus	Tensile modulus	ISO 527-2	2400 Mpa
Tensile modulus	Tensile modulus	Tensile modulus	ASTM D638	2500 Mpa
Ball Pressure Test	Ball Pressure Test	ISO 2039-1	102 Mpa
Bending modulus	Bending modulus	ASTM D790	2400 Mpa
Bending modulus	Bending modulus	Bending modulus	ISO 178	2400 Mpa
bending strength	bending strength	ASTM D790	77.2 Mpa

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Vicat softening temperature	Vicat softening temperature --	ISO 306/B50	106 °C
Vicat softening temperature	Vicat softening temperature	Vicat softening temperature --	ISO 306/A50	115 °C
Hot deformation temperature	Hot deformation temperature 1.8MPa,Annealed	ISO 75-2/A	99.0 °C
Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 0.45MPa,Annealed	ISO 75-2/B	107 °C
Maximum operating temperature	Maximum operating temperature		85 °C
thermal conductivity	thermal conductivity	DIN 52612	0.17 W/m/K
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion MD	ISO 11359-2	9E-05 cm/cm/°C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Water absorption rate	Water absorption rate Equilibrium,23°C,50%RH	ISO 62	0.25 %
Shrinkage rate	Shrinkage rate	ISO 294-4	0.40-0.70 %
Shrinkage rate	Shrinkage rate	Shrinkage rate MD	ASTM D955	0.55 %
Melt Volume Flow Rate (MVR)	Melt Volume Flow Rate (MVR) 220°C/10.0kg	ISO 1133	7.00 cm3/10min
melt mass-flow rate	melt mass-flow rate 220°C/10.0kg	ASTM D1238	7.0 g/10min

Electrical performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Compared to the anti leakage trace index	Compared to the anti leakage trace index	IEC 60112	V
Dielectric strength	Dielectric strength 1.50mm	IEC 60243-1	39 KV/mm
Volume resistivity	Volume resistivity	IEC 60093	1E+15 ohms·cm
Volume resistivity	Volume resistivity	Volume resistivity	ASTM D257	>1.0E+15 ohms·cm

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.