PA+PP Latiblend 6252 H2 G/30 LATI S.p.A.

Shrinkage rate

MD:2.00mm

Shrinkage rate

TD:2.00mm

Tensile modulus

150°C

Tensile modulus

120°C

Tensile modulus

90°C

Tensile modulus

60°C

Tensile modulus

23°C

Water absorption rate

23°C,24hr

tensile strength

Break,60°C

tensile strength

Break,23°C

tensile strength

Yield,150°C

tensile strength

Yield,120°C

tensile strength

Yield,90°C

Impact strength of simply supported beam without notch

-20°C

Charpy Notched Impact Strength

23°C

Charpy Notched Impact Strength

-20°C

Tensile strain

Break,150°C

UL flame retardant rating

0.75mm

Linear coefficient of thermal expansion

MD：30to100°C

Vicat softening temperature

Continuous use temperature

Hot deformation temperature

1.8MPa,Unannealed

Hot deformation temperature

0.45MPa,Unannealed

Impact strength of simply supported beam without notch

23°C

tensile strength

Yield,60°C

Tensile strain

Yield,120°C

Tensile strain

Yield,150°C

Tensile strain

Break,23°C

Tensile strain

Break,60°C

Tensile strain

Break,90°C

Tensile strain

Break,120°C

tensile strength

Break,90°C

tensile strength

Break,120°C

tensile strength

Break,150°C

Tensile strain

Yield,60°C

Tensile strain

Yield,90°C

density