mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Poisson's ratio	Poisson's ratio	Internal Method	0.30
MatrixCrazingStrain	MatrixCrazingStrain	Internal Method	0.60 %
tensile strength	tensile strength Yield,Compression Molded	ISO 527-2	150 MPa
Tensile strain	Tensile strain Break,Compression Molded	ISO 527-2	1.6 %
Bending modulus	Bending modulus Compression Molded	ISO 178	13000 MPa
bending strength	bending strength Compression Molded	ISO 178	280 MPa
Compressive stress	Compressive stress	ISO 14126	120 MPa
Tensile modulus	Tensile modulus Compression Molded	ISO 527-2	13000 MPa

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed	ISO 75-2/A	>200 °C
Continuous use temperature	Continuous use temperature	Internal Method	170 °C
Glass transition temperature	Glass transition temperature	DSC	162 °C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion MD	ISO 11359-2	1.2E-05 cm/cm/°C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
density	density	ISO 1183	1.80 g/cm³
Shrinkage rate	Shrinkage rate --	ISO 2577	0.040 %
Shrinkage rate	Shrinkage rate	Shrinkage rate --3	DIN 53464	0.0 %
Water absorption rate	Water absorption rate Saturation,23°C	ISO 62	<0.30 %

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.