mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Bending modulus	Bending modulus	ISO 178	3500 MPa
Nominal fracture strain	Nominal fracture strain	ISO 527-22	2.0 %
Tensile strain	Tensile strain Break	ISO 527-2/5	2.0 %
Tensile strain	Tensile strain	Tensile strain Yield	ISO 527-22	2.0 %
tensile strength	tensile strength Yield	ISO 527-22	42.0 MPa
tensile strength	tensile strength	tensile strength Yield	ISO 527-2/5	43.0 MPa
Tensile modulus	Tensile modulus	ISO 527-22	3300 MPa
bending strength	bending strength	ISO 178	80.0 MPa

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Hot deformation temperature	Hot deformation temperature 0.45MPa	ISO 75-22	82.0 °C
Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 0.45MPa,Annealed	ISO 75-2/B	86.0 °C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion TD	ISO 11359-22	8E-05 cm/cm/°C
Hot deformation temperature	Hot deformation temperature 1.8MPa,Annealed	ISO 75-2/A	82.0 °C
Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 1.8MPa	ISO 75-22	71.0 °C
Vicat softening temperature	Vicat softening temperature --	ISO 306/A120	93.0 °C
	Vicat softening temperature	Vicat softening temperature --	ISO 306/B50	86.0 °C
	Vicat softening temperature	Vicat softening temperature	Vicat softening temperature 50N	ISO 3062	86.0 °C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion MD	ISO 11359-22	8E-05 cm/cm/°C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
viscosity	viscosity	ISO 307	91.0 cm³/g
Water absorption rate	Water absorption rate Equilibrium	ISO 622	0.0 %
Water absorption rate	Water absorption rate	Water absorption rate Saturation	ISO 622	0.0 %
Melt Volume Flow Rate (MVR)	Melt Volume Flow Rate (MVR) 200°C/5.0kg	ISO 11332	11.0 cm³/10min
melt mass-flow rate	melt mass-flow rate 200°C/5.0kg	ISO 1133	11 g/10min
Apparent density	Apparent density	ISO 60	0.60 g/cm³
density	density	ISO 11832	1050 kg/m³
density	density	density	ISO 1183	1.05 g/cm³

Electrical performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Dissipation factor	Dissipation factor 1MHz	IEC 602502	6E-05
	Dissipation factor	Dissipation factor 100Hz	IEC 602502	9E-05
	Dissipation factor	Dissipation factor	Dissipation factor 1MHz	ASTM D150	6E-05
Relative permittivity	Relative permittivity 100Hz	IEC 602502	2.50
Dielectric strength	Dielectric strength	IEC 60243-12	140 kV/mm
Relative permittivity	Relative permittivity 1MHz	IEC 602502	2.50
Volume resistivity	Volume resistivity	IEC 600932	>1.0E+15 ohms·m
Surface resistivity	Surface resistivity	IEC 600932	1E+13 ohms

hardness	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Ball Pressure Test	Ball Pressure Test	ISO 2039-1	150 MPa
Rockwell hardness	Rockwell hardness R-Scale	ISO 2039-2	105

hardness

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Ball Pressure Test

ISO 2039-1

150 MPa

Rockwell hardness

R-Scale

ISO 2039-2

105

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.