mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Tensile modulus	Tensile modulus --3	ASTM D638	2250 Mpa
	Tensile modulus	Tensile modulus --4	ASTM D638	2250 Mpa
	Tensile modulus	Tensile modulus	Tensile modulus --	ISO 527-2/1	2050 Mpa
tensile strength	tensile strength Yield5	ASTM D638	53.0 Mpa
	tensile strength	tensile strength Yield	ISO 527-2/50	50.0 Mpa
		tensile strength	tensile strength Break5	ASTM D638	51.0 Mpa
		tensile strength	tensile strength	tensile strength Break	ISO 527-2/50	50.0 Mpa
elongation	elongation Yield5	ASTM D638	4.0 %
	elongation	elongation Yield	ISO 527-2/50	4.0 %
		elongation	elongation Break5	ASTM D638	120 %
		elongation	elongation	elongation Break	ISO 527-2/50	120 %
Bending modulus	Bending modulus 50.0 mm Span6	ASTM D790	2030 Mpa
Bending modulus	Bending modulus	Bending modulus --7	ISO 178	2000 Mpa
bending strength	bending strength --7,8	ISO 178	80.0 Mpa
bending strength	bending strength	bending strength Yield, 50.0 mm Span6	ASTM D790	84.0 Mpa

injection	Điều kiện kiểm tra	Kết quả kiểm tra
drying temperature	drying temperature	110 °C
drying time	drying time	4.0 to 6.0 hr
Suggested maximum moisture content	Suggested maximum moisture content	0.020 %
Suggested injection volume	Suggested injection volume	50 to 80 %
Temperature at the rear of the barrel	Temperature at the rear of the barrel	245 to 265 °C
Temperature in the middle of the barrel	Temperature in the middle of the barrel	250 to 270 °C
Temperature at the front of the material cylinder	Temperature at the front of the material cylinder	255 to 275 °C
Spray nozzle temperature	Spray nozzle temperature	255 to 270 °C
Processing (melt) temperature	Processing (melt) temperature	260 to 275 °C
Mold temperature	Mold temperature	65 to 90 °C
Back pressure	Back pressure	0.300 to 0.700 Mpa
Screw speed	Screw speed	50 to 80 rpm
Exhaust hole depth	Exhaust hole depth	0.013 to 0.020 mm

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Hot deformation temperature	Hot deformation temperature 0.45 MPa, Unannealed, 6.40 mm	ASTM D648	107 °C
	Hot deformation temperature	Hot deformation temperature 1.8 MPa, Unannealed, 3.20 mm	ASTM D648	84.0 °C
		Hot deformation temperature	Hot deformation temperature 1.8 MPa, Unannealed, 6.40 mm	ASTM D648	99.0 °C
		Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span10	ISO 75-2/Af	75.0 °C
Vicat softening temperature	Vicat softening temperature --	ASTM D152511	122 °C
	Vicat softening temperature	Vicat softening temperature --	ISO 306/B50	120 °C
	Vicat softening temperature	Vicat softening temperature	Vicat softening temperature --	ISO 306/B120	125 °C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion Flow : -40 to 40°C	ASTM E831	9.5E-5 cm/cm/°C
	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion Across Flow : -40 to 40°C	ASTM E831	9.0E-5 cm/cm/°C
	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion Across Flow : -40°C	ISO 11359-2	9.0E-5 cm/cm/°C
RTI Elec	RTI Elec	UL 746	75.0 °C
RTI Imp	RTI Imp	UL 746	75.0 °C
RTI	RTI	UL 746	75.0 °C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Specific volume	Specific volume	ASTM D792	0.830 cm³/g
melt mass-flow rate	melt mass-flow rate 250°C/5.0 kg	ISO 1133	16 g/10 min
Melt Volume Flow Rate (MVR)	Melt Volume Flow Rate (MVR) 250°C/5.0 kg	ISO 1133	15.0 cm3/10min
Shrinkage rate	Shrinkage rate Flow : 3.20 mm	Internal Method	0.80 - 1.0 %
Shrinkage rate	Shrinkage rate	Shrinkage rate Across FlowFlow 2	Internal Method	0.80 - 1.0 %
Water absorption rate	Water absorption rate Saturation, 23°C	ISO 62	0.50 %
Water absorption rate	Water absorption rate	Water absorption rate Equilibrium, 23°C, 50% RH	ISO 62	0.15 %
Outdoor applicability	Outdoor applicability	UL 746C	f2

Electrical performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Arc resistance	Arc resistance	ASTM D495	PLC 5
Compared to the anti leakage trace index	Compared to the anti leakage trace index	UL 746	PLC 1
High arc combustion index	High arc combustion index	UL 746	PLC 0
High voltage arc tracing rate	High voltage arc tracing rate	UL 746	PLC 0
Hot wire ignition	Hot wire ignition	UL 746	PLC 3

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.