PP LNP™ STAT-KON™ ME003S compound SABIC

So sánh

Bảng thông số kỹ thuật

impact performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength 23°C3	ISO 180/1U	8.6 kJ/m²
Dart impact	Dart impact 23°C,EnergyatPeakLoad	ASTM D3763	14.8 J
Dart impact	Dart impact	Dart impact --	ISO 6603-2	3.20 J
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C	ASTM D256	16 J/m
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C3	ISO 180/1A	1.8 kJ/m²
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength 23°C	ASTM D4812	130 J/m

mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Tensile modulus	Tensile modulus --2	ASTM D638	8960 MPa
Tensile modulus	Tensile modulus	Tensile modulus --	ISO 527-2/1	8590 MPa
tensile strength	tensile strength Yield	ASTM D638	47.6 MPa
	tensile strength	tensile strength Yield	ISO 527-2	47.0 MPa
		tensile strength	tensile strength Break	ASTM D638	39.3 MPa
		tensile strength	tensile strength	tensile strength Break	ISO 527-2	44.0 MPa
elongation	elongation Yield	ASTM D638	0.70 %
	elongation	elongation Yield	ISO 527-2	0.78 %
		elongation	elongation Break	ASTM D638	1.3 %
		elongation	elongation	elongation Break	ISO 527-2	1.0 %
Bending modulus	Bending modulus --	ASTM D790	6890 MPa
Bending modulus	Bending modulus	Bending modulus --	ISO 178	7000 MPa
bending strength	bending strength --	ASTM D790	65.5 MPa
bending strength	bending strength	bending strength --	ISO 178	62.0 MPa

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Hot deformation temperature	Hot deformation temperature 0.45MPa,Unannealed,3.20mm	ASTM D648	154 °C
	Hot deformation temperature	Hot deformation temperature 0.45MPa,Unannealed,64.0mmSpan4	ISO 75-2/Bf	150 °C
		Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed,3.20mm	ASTM D648	134 °C
		Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed,64.0mmSpan4	ISO 75-2/Af	131 °C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion MD:-40to40°C	ASTME831	7E-05 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion TD:-40to40°C	ASTME831	2.9E-05 cm/cm/°C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Shrinkage rate	Shrinkage rate TD:24hr	ISO 294-4	0.60 %
Shrinkage rate	Shrinkage rate	Shrinkage rate MD:24hr	ISO 294-4	0.52 %
density	density	ASTMD792	0.990 g/cm³
Shrinkage rate	Shrinkage rate MD:24hr	ASTM D955	0.40to0.60 %
Shrinkage rate	Shrinkage rate	Shrinkage rate TD:24hr	ASTM D955	0.50to0.70 %

Electrical performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Surface resistivity	Surface resistivity	ASTM D257	1E+02 ohms

Electrical performance

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Surface resistivity

ASTM D257

1E+02 ohms

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.