ABS KumhoSunny ABS HU650SK-P Shanghai KumhoSunny Plastics Co., Ltd.

So sánh

Bảng thông số kỹ thuật

impact performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Charpy Notched Impact Strength	Charpy Notched Impact Strength -30°C	ISO 179	11 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch 23°C	ISO 179	无断裂
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C	ISO 180	20 kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap -30°C	ISO 180	10 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch -30°C	ISO 179	无断裂
Charpy Notched Impact Strength	Charpy Notched Impact Strength 23°C	ISO 179	22 kJ/m²
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength 23°C	ISO 180	无断裂
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength -30°C	ISO 180	无断裂

mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Poisson's ratio	Poisson's ratio	ISO 527	0.39
bending strength	bending strength 64.0mm	ISO 178	65.0 MPa
Bending modulus	Bending modulus 64.0mm	ISO 178	2360 MPa
Tensile strain	Tensile strain Break	ISO 527-2/50	65 %
tensile strength	tensile strength	ISO 527-2/50	40.0 MPa

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion TD:-40to40°C	ISO 11359-2	7.6E-05 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion MD:-40to40°C	ISO 11359-2	7.7E-05 cm/cm/°C
Vicat softening temperature	Vicat softening temperature	ISO 306/B50	115 °C
Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed	ISO 75-2/A	95.0 °C
Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 0.45MPa,Unannealed	ISO 75-2/B	111 °C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Shrinkage rate	Shrinkage rate 23°C	ISO 294-4	0.40to0.70 %
density	density 23°C	ISO 1183	1.06 g/cm³
melt mass-flow rate	melt mass-flow rate 220°C/10.0kg	ISO 1133	4.0 g/10min

Physical properties

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Shrinkage rate

23°C

ISO 294-4

0.40to0.70 %

density

23°C

ISO 1183

1.06 g/cm³

melt mass-flow rate

220°C/10.0kg

ISO 1133

4.0 g/10min

Electrical performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Volume resistivity	Volume resistivity	IEC 60093	1E+15 ohms·cm
Surface resistivity	Surface resistivity	IEC 60093	1E+15 ohms

Electrical performance

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Volume resistivity

IEC 60093

1E+15 ohms·cm

Surface resistivity

IEC 60093

1E+15 ohms

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.