mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Bending modulus	Bending modulus	ASTM D790	1080 Mpa
elongation	elongation Break	ASTM D638	>800 %
tensile strength	tensile strength Break	ASTM D638	26.5 Mpa
elongation	elongation Break	ASTM D-638	>800 %
tensile strength	tensile strength Break	ASTM D-638	26.5 Mpa
Bending modulus	Bending modulus	ASTM D790/ISO 178	1080 kg/cm²(MPa)[Lb/in²]
Rockwell hardness	Rockwell hardness	ASTM D785	-
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	ASTM D256/ISO 179	3.6 kg·cm/cm(J/M)ft·lb/in

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Melting temperature	Melting temperature	Internal Method	145 °C
Hot deformation temperature	Hot deformation temperature 0.45MPa,Unannealed	ASTM D648	105 °C
Melting temperature	Melting temperature		145 °C
Hot deformation temperature	Hot deformation temperature HDT	ASTM D648/ISO 75	105 ℃（℉）

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
melt mass-flow rate	melt mass-flow rate	ASTM D1238	20 g/10min
melt mass-flow rate	melt mass-flow rate	ASTM D1238/ISO 1133	20 g/10min
density	density	ASTM D792/ISO 1183	0.9

Physical properties

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

melt mass-flow rate

ASTM D1238

20 g/10min

melt mass-flow rate

ASTM D1238/ISO 1133

20 g/10min

density

ASTM D792/ISO 1183

0.9

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.