| Impact strength of cantilever beam gap | Impact strength of cantilever beam gap -30°C | ISO 180/A | 3.0 kJ/m² |
| Impact strength of cantilever beam gap | Impact strength of cantilever beam gap 23°C | ISO 180/A | 6.0 kJ/m² |
| Ball Pressure Test | Ball Pressure Test | ISO 2039-1 | 95.0 MPa |
| Hot deformation temperature | Hot deformation temperature 0.45MPa,Annealed | ISO 75-2/B | 105 °C |
| density | density | ISO 1183 | 1.12 g/cm³ |
| Melt Volume Flow Rate (MVR) | Melt Volume Flow Rate (MVR) 240°C/10.0kg | ISO 1133 | 30.0 cm³/10min |
| Shrinkage rate | Shrinkage rate | ISO 294-4 | 0.60 % |
| Water absorption rate | Water absorption rate Equilibrium,23°C,50%RH | ISO 62 | 1.1 % |
| Tensile modulus | Tensile modulus | ISO 527-2 | 3300 MPa |
| tensile strength | tensile strength Yield,23°C | ISO 527-2 | 55.0 MPa |
| Tensile strain | Tensile strain Yield,23°C | ISO 527-2 | 3.0 % |
| Bending modulus | Bending modulus | ISO 178 | 2850 MPa |
| Hot deformation temperature | Hot deformation temperature 1.8MPa,Annealed | ISO 75-2/A | 80.0 °C |
| Vicat softening temperature | Vicat softening temperature -- | ISO 306/A50 | 170 °C |
| Vicat softening temperature | Vicat softening temperature -- | ISO 306/B50 | 108 °C |
| Linear coefficient of thermal expansion | Linear coefficient of thermal expansion MD | ISO 11359-2 | 6E-05 cm/cm/°C |
| Surface resistivity | Surface resistivity | IEC 60093 | 1E+14 ohms |
| Volume resistivity | Volume resistivity | IEC 60093 | 1E+15 ohms·cm |
| Relative permittivity | Relative permittivity 1MHz | IEC 60250 | 2.90 |
| Dissipation factor | Dissipation factor 1MHz | IEC 60250 | 0.013 |
| bending strength | bending strength | ISO 178 | 80.0 MPa |
| elongation | elongation Break | ISO 527-3 | 4.0 % |
| Charpy Notched Impact Strength | Charpy Notched Impact Strength -30°C | ISO 179 | 3.0 kJ/m² |
| Charpy Notched Impact Strength | Charpy Notched Impact Strength 23°C | ISO 179 | 8.0 kJ/m² |
| Impact strength of simply supported beam without notch | Impact strength of simply supported beam without notch -30°C | ISO 179 | 25 kJ/m² |
| Impact strength of simply supported beam without notch | Impact strength of simply supported beam without notch 23°C | ISO 179 | 35 kJ/m² |