Polyester Hytrel® HTR8341C BK320 DUPONT USA

So sánh

Bảng thông số kỹ thuật

impact performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch 23°C	ISO 179/1eU	NoBreak
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C	ISO 8256/1	300 kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C	ISO 180/1A	NoBreak
Charpy Notched Impact Strength	Charpy Notched Impact Strength -40°C,PartialBreak2	ISO 179/1eA	NoBreak
Charpy Notched Impact Strength	Charpy Notched Impact Strength	Charpy Notched Impact Strength 23°C	ISO 179/1eA	NoBreak
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch -30°C	ISO 179/1eU	NoBreak

flammability	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Burning rate	Burning rate 1.00mm	ISO 3795	<100 mm/min
FMVSS flammability	FMVSS flammability	FMVSS302	B

flammability

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Burning rate

1.00mm

ISO 3795

<100 mm/min

FMVSS flammability

FMVSS302

elastomer	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
tear strength	tear strength 横向Flow	ISO 34-1	120 kN/m
tear strength	tear strength Flow	ISO 34-1	110 kN/m

elastomer

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

tear strength

横向Flow

ISO 34-1

120 kN/m

tear strength

Flow

ISO 34-1

110 kN/m

mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Tensile strain	Tensile strain Break	ISO 527-2	>300 %
Nominal tensile fracture strain	Nominal tensile fracture strain	ISO 527-2	350 %
Bending modulus	Bending modulus	ISO 178	80.0 MPa
Tensile modulus	Tensile modulus	ISO 527-2	80.0 MPa
tensile strength	tensile strength Break	ISO 527-2	28.0 MPa
	tensile strength	tensile strength 10%Strain	ISO 527-2	7.00 MPa
		tensile strength	tensile strength 50%Strain	ISO 527-2	12.0 MPa
			tensile strength	tensile strength 100%Strain	ISO 527-2	13.0 MPa
			tensile strength	tensile strength	tensile strength 300%Strain	ISO 527-2	23.0 MPa

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion TD：EffectiveThermalDiffusivity	ISO 11359-2	5.44E-08 m²/s
	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion TD：-40to23°C	ISO 11359-2	2.4E-04 cm/cm/°C
		Linear coefficient of thermal expansion	Linear coefficient of thermal expansion TD：--	ISO 11359-2	2E-04 cm/cm/°C
		Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion MD：-40to23°C	ISO 11359-2	2.3E-04 cm/cm/°C
PeakCrystallizationTemperature	PeakCrystallizationTemperature	ISO 11357-3	167 °C
Melting temperature	Melting temperature	ISO 11357-3	207 °C
Glass transition temperature	Glass transition temperature	ISO 11357-2	-70.0 °C
Brittle temperature	Brittle temperature	ISO 974	-100 °C
Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed	ISO 75-2/A	42.0 °C
Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 0.45MPa,Unannealed	ISO 75-2/B	56.0 °C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion MD：--	ISO 11359-2	1.7E-04 cm/cm/°C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Water absorption rate	Water absorption rate Equilibrium,23°C,2.00mm,50%RH	ISO 62	0.20 %
Water absorption rate	Water absorption rate	Water absorption rate Saturation,23°C,2.00mm	ISO 62	0.50 %
melt mass-flow rate	melt mass-flow rate 230°C/2.16kg	ISO 1133	0.90 g/10min
density	density	ISO 1183	1.14 g/cm³

Electrical performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Dissipation factor	Dissipation factor 1MHz	IEC 60250	9.5E-03
Dissipation factor	Dissipation factor	Dissipation factor 100Hz	IEC 60250	0.030
Dielectric strength	Dielectric strength	IEC 60243-1	19 kV/mm
Volume resistivity	Volume resistivity	IEC 60093	8E+12 ohms·cm
Surface resistivity	Surface resistivity	IEC 60093	4E+14 ohms
Compared to the anti leakage trace index	Compared to the anti leakage trace index	IEC 60112	PLC 0

hardness	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Shore hardness	Shore hardness ShoreD,15Sec	ISO 868	37
Shore hardness	Shore hardness ShoreD	ISO 868	40

hardness

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Shore hardness

ShoreD,15Sec

ISO 868

Shore hardness

ShoreD

ISO 868

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.