PC LUBEXAN 1522 FR NATURAL LUBEN PLAST srl

So sánh

Bảng thông số kỹ thuật

impact performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength 23°C	ISO 180	无断裂
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C	ASTM D256	无断裂
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch 23°C	ISO 179/1eU	无断裂

impact performance

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Suspended wall beam without notch impact strength

23°C

ISO 180

无断裂

Impact strength of cantilever beam gap

23°C

ASTM D256

无断裂

Impact strength of simply supported beam without notch

23°C

ISO 179/1eU

无断裂

flammability	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Burning wire flammability index	Burning wire flammability index 2.0mm	IEC 60695-2-12	960 °C
UL flame retardant rating	UL flame retardant rating 3.2mm	UL 94	V-0

flammability

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Burning wire flammability index

2.0mm

IEC 60695-2-12

960 °C

UL flame retardant rating

3.2mm

UL 94

V-0

mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
bending strength	bending strength	ISO 178	50.0to60.0 MPa
tensile strength	tensile strength Yield	ISO 527-2/1A/50	55.0to65.0 MPa
Tensile modulus	Tensile modulus	ISO 527-2/1A/1	2500to2800 MPa
Bending modulus	Bending modulus	ISO 178	2000to2300 MPa
Tensile strain	Tensile strain Break	ISO 527-2/1A/50	20to25 %
Tensile strain	Tensile strain	Tensile strain Yield	ISO 527-2/1A/50	5.0to10 %
tensile strength	tensile strength Break	ISO 527-2/1A/50	40.0to50.0 MPa

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Vicat softening temperature	Vicat softening temperature --	ISO 306/B120	130to140 °C
Vicat softening temperature	Vicat softening temperature	Vicat softening temperature --	ISO 306/A120	135to145 °C
Glass transition temperature	Glass transition temperature	Internal Method	140to150 °C
Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed,3.20mm	ASTM D648	125to135 °C
	Hot deformation temperature	Hot deformation temperature 0.45MPa,Unannealed	ISO 75-2/B	135to145 °C
	Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 0.45MPa,Unannealed,3.20mm	ASTM D648	130to140 °C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Water absorption rate	Water absorption rate Saturation,23°C,3.20mm	ISO 62	0.36 %
Water absorption rate	Water absorption rate	Water absorption rate 23°C,24hr,3.20mm	ISO 62	0.15 %
melt mass-flow rate	melt mass-flow rate 300°C/1.2kg	ISO 1133	15to22 g/10min
density	density	ISO 1183/A	1.18to1.22 g/cm³

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.