Unspecified LUBLENE GK30 NATURAL LUBEN PLAST srl

So sánh

Bảng thông số kỹ thuật

impact performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Charpy Notched Impact Strength	Charpy Notched Impact Strength 23°C	ISO 179/1eA	3.0to4.0 kJ/m²
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength 23°C	ISO 180	20to30 kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C	ISO 180/A	3.0to4.0 kJ/m²
	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C4	ASTM D256	2.5to3.5 kJ/m²
		Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C3	ASTM D256	20to30 kJ/m²
		Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C,3.20mm	ASTM D256A	25to35 J/m
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch 23°C	ISO 179/1eU	20to30 kJ/m²

mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
bending strength	bending strength	ISO 178	30.0to40.0 MPa
Tensile strain	Tensile strain Yield	ISO 527-2/1A/5	4.0to5.0 %
tensile strength	tensile strength Break	ISO 527-2/1A/5	18.0to22.0 MPa
tensile strength	tensile strength	tensile strength Yield	ISO 527-2/1A/5	23.0to27.0 MPa
Tensile modulus	Tensile modulus	ISO 527-2/1A/1	2000to3000 MPa
Bending modulus	Bending modulus	ISO 178	1500to2500 MPa
Tensile strain	Tensile strain Break	ISO 527-2/1A/5	25to30 %

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Hot deformation temperature	Hot deformation temperature 0.45MPa,Unannealed,3.20mm	ASTM D648	120to130 °C
Melting temperature	Melting temperature	Internal Method	165to170 °C
Vicat softening temperature	Vicat softening temperature --	ISO 306/B120	95.0to105 °C
Vicat softening temperature	Vicat softening temperature	Vicat softening temperature --	ISO 306/A120	100to110 °C
Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed,3.20mm	ASTM D648	60.0to70.0 °C
Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 0.45MPa,Unannealed	ISO 75-2/B	125to135 °C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
density	density	ISO 1183/A	1.10to1.14 g/cm³

Physical properties

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

density

ISO 1183/A

1.10to1.14 g/cm³

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.