PC XANTAR® C CM 206 Mitsubishi Chemical Corporation
So sánhBảng thông số kỹ thuật
| impact performance | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| Impact strength of cantilever beam gap | Impact strength of cantilever beam gap -40°C | ISO 180/4A | 15 kJ/m² |
| Impact strength of cantilever beam gap | Impact strength of cantilever beam gap -20°C | ISO 180/4A | 30 kJ/m² |
| Impact strength of cantilever beam gap | Impact strength of cantilever beam gap 23°C | ISO 180/4A | 65 kJ/m² |
| Charpy Notched Impact Strength | Charpy Notched Impact Strength -30°C | ISO 179/1eA | 15 kJ/m² |
| Charpy Notched Impact Strength | Charpy Notched Impact Strength 23°C | ISO 179/1eA | 35 kJ/m² |
| Impact strength of simply supported beam without notch | Impact strength of simply supported beam without notch -30°C | ISO 179/1eU | NoBreak |
| Impact strength of simply supported beam without notch | Impact strength of simply supported beam without notch 23°C | ISO 179/1eU | NoBreak |
| flammability | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| Burning wire flammability index | Burning wire flammability index 3.0mm | IEC 60695-2-12 | 675 °C |
| Hot filament ignition temperature | Hot filament ignition temperature 1.5mm | IEC 60695-2-13 | 700 °C |
| Hot filament ignition temperature | Hot filament ignition temperature 3.0mm | IEC 60695-2-13 | 700 °C |
| Extreme Oxygen Index | Extreme Oxygen Index | ISO 4589-2 | 21 % |
| UL flame retardant rating | UL flame retardant rating 1.5mm | IEC 60695-11-10,-20 | HB |
| UL flame retardant rating | UL flame retardant rating 3.0mm | IEC 60695-11-10,-20 | HB |
| Burning wire flammability index | Burning wire flammability index 1.5mm | IEC 60695-2-12 | 675 °C |
| mechanical properties | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| Tensile modulus | Tensile modulus | ISO 527-2 | 2100 MPa |
| tensile strength | tensile strength Yield | ISO 527-2 | 45.0 MPa |
| Tensile strain | Tensile strain Yield | ISO 527-2 | 4.0 % |
| Nominal tensile fracture strain | Nominal tensile fracture strain | ISO 527-2 | >50 % |
| Bending modulus | Bending modulus | ISO 178 | 2200 MPa |
| bending strength | bending strength | ISO 178 | 75.0 MPa |
| thermal performance | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| Hot deformation temperature | Hot deformation temperature 1.8MPa,Unannealed | ISO 75-2/A | 95.0 °C |
| Vicat softening temperature | Vicat softening temperature | ISO 306/B50 | 110 °C |
| Linear coefficient of thermal expansion | Linear coefficient of thermal expansion MD | ISO 11359-2 | 7E-05 cm/cm/°C |
| Linear coefficient of thermal expansion | Linear coefficient of thermal expansion TD | ISO 11359-2 | 7E-05 cm/cm/°C |
| Physical properties | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| Shrinkage rate | Shrinkage rate MD | ISO 294-4 | 0.60 % |
| Water absorption rate | Water absorption rate Saturation,23°C | ISO 62 | 0.70 % |
| density | density | ISO 1183 | 1.12 g/cm³ |
| Melt Volume Flow Rate (MVR) | Melt Volume Flow Rate (MVR) 260°C/5.0kg | ISO 1133 | 40.0 cm³/10min |
| ThermalConductivityofMelt | ThermalConductivityofMelt | 0.22 W/m/K |
| Electrical performance | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| Surface resistivity | Surface resistivity | IEC 60093 | >1.0E+15 ohms |
| Volume resistivity | Volume resistivity | IEC 60093 | >1.0E+15 ohms·cm |
| Dielectric strength | Dielectric strength | IEC 60243-1 | 35 kV/mm |
| Relative permittivity | Relative permittivity 1MHz | IEC 60250 | 2.90 |
| Compared to the anti leakage trace index | Compared to the anti leakage trace index CTI | UL 746 | PLC 0 |
| Compared to the anti leakage trace index | Compared to the anti leakage trace index | IEC 60112 | PLC 2 |