PBT TV4 240 DSM Additive Manufacturing

So sánh

Bảng thông số kỹ thuật

impact performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Charpy Notched Impact Strength	Charpy Notched Impact Strength -30°C	ISO 179/1eA	7.0 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	Charpy Notched Impact Strength 23°C	ISO 179/1eA	7.0 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch -30°C	ISO 179/1eU	40 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch 23°C	ISO 179/1eU	40 kJ/m²

flammability	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
UL flame retardant rating	UL flame retardant rating 0.75mm	IEC 60695-11-10,-20	HB
UL flame retardant rating	UL flame retardant rating 1.5mm	IEC 60695-11-10,-20	HB
Extreme Oxygen Index	Extreme Oxygen Index	ISO 4589-2	20 %

flammability

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

UL flame retardant rating

0.75mm

IEC 60695-11-10,-20

UL flame retardant rating

1.5mm

IEC 60695-11-10,-20

Extreme Oxygen Index

ISO 4589-2

20 %

mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Tensile strain	Tensile strain Break	ISO 527-2	2.7 %
Tensile modulus	Tensile modulus	ISO 527-2	7200 MPa
tensile strength	tensile strength Break	ISO 527-2	120 MPa

mechanical properties

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Tensile strain

Break

ISO 527-2

2.7 %

Tensile modulus

ISO 527-2

7200 MPa

tensile strength

Break

ISO 527-2

120 MPa

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Hot deformation temperature	Hot deformation temperature 0.45MPa,Unannealed	ISO 75-2/B	220 °C
Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed	ISO 75-2/A	205 °C
Melting temperature	Melting temperature	ISO 11357-3	225 °C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion MD	ISO 11359-2	4E-05 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion TD	ISO 11359-2	8E-05 cm/cm/°C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
density	density	ISO 1183	1.45 g/cm³
Melt Volume Flow Rate (MVR)	Melt Volume Flow Rate (MVR) 250°C/2.16kg	ISO 1133	23.0 cm³/10min
Shrinkage rate	Shrinkage rate TD	ISO 294-4	1.3 %
Shrinkage rate	Shrinkage rate	Shrinkage rate MD	ISO 294-4	0.45 %
Water absorption rate	Water absorption rate Saturation,23°C	ISO 62	0.30 %
Water absorption rate	Water absorption rate	Water absorption rate Equilibrium,23°C,50%RH	ISO 62	0.15 %

Electrical performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Dissipation factor	Dissipation factor 1MHz	IEC 60250	0.018
Compared to the anti leakage trace index	Compared to the anti leakage trace index	IEC 60112	PLC 1
Relative permittivity	Relative permittivity 100Hz	IEC 60250	3.70
Relative permittivity	Relative permittivity	Relative permittivity 1MHz	IEC 60250	3.50
Dissipation factor	Dissipation factor 100Hz	IEC 60250	2E-03
Volume resistivity	Volume resistivity	IEC 60093	>1.0E+15 ohms·cm
Dielectric strength	Dielectric strength	IEC 60243-1	30 kV/mm

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.