mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Tensile modulus	Tensile modulus	ISO 527-1	2400 Mpa
Tensile stress	Tensile stress Yield	ISO 527-1	49.0 Mpa
Tensile strain	Tensile strain Yield	ISO 527-1	3.0 %
Fracture strain	Fracture strain 23℃	ISO 527-1	>15 %
Bending modulus	Bending modulus 23℃	ISO 178	2300 Mpa
bending strength	bending strength 23℃	ISO 178	77.0 Mpa
Charpy Notched Impact Strength	Charpy Notched Impact Strength 23℃	ISO 179/1eA	30.0 KJ/m
	Charpy Notched Impact Strength	Charpy Notched Impact Strength -30℃	ISO 179/1eA	12.0 KJ/m
		Charpy Notched Impact Strength	Charpy Notched Impact Strength 23℃	ISO 179/1eU	220 KJ/m
		Charpy Notched Impact Strength	Charpy Notched Impact Strength	Charpy Notched Impact Strength -30℃	ISO 179/1eU	160 KJ/m
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap -30℃	ISO 180/1A	12.0 KJ/m
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23℃	ISO 180/1A	30.0 KJ/m
Shore hardness	Shore hardness	ISO 2039-1	105 Mpa

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Hot deformation temperature	Hot deformation temperature 0.45MPa	ISO 75-1	106 °C
Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 1.80MPa	ISO 75-1	99.0 °C
Vicat softening temperature	Vicat softening temperature 50℃/h 50N	ISO 306	105 °C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion parallel	ISO 11359-1	0.000080 cm/cm℃

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Shrinkage rate	Shrinkage rate	ISO 294-4	0.50-0.70 %

Physical properties

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Shrinkage rate

ISO 294-4

0.50-0.70 %

Electrical performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Dielectric strength	Dielectric strength	IEC 60243-1	38 KV/mm
Surface resistivity	Surface resistivity	IEC 60093	1E+16 ohms
Volume resistivity	Volume resistivity	IEC 60093	1E+14 ohm.m
Relative permittivity	Relative permittivity 100Hz	IEC 60250	3.10
Relative permittivity	Relative permittivity	Relative permittivity 1000Hz	IEC 60250	3.00
Dielectric loss	Dielectric loss 100Hz	IEC 60250	0.0050
Dielectric loss	Dielectric loss	Dielectric loss 1000Hz	IEC 60250	0.0090

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.