PC CALIBRE™ MEGARAD™ 2081-15 STYRON US
- Đặc tính:Lớp y tế
- Lĩnh vực ứng dụng:Sản phẩm y tếSản phẩm chăm sóc
So sánh
Xem giáBảng thông số kỹ thuật
| optical performance | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| Refractive index | Refractive index | ASTMD542 | 1.586 |
| transmissivity | transmissivity | ASTM D1003 | 89.0 % |
| turbidity | turbidity | ASTM D1003 | 1.0 % |
| impact performance | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| Dart impact | Dart impact 23°C,总能量 | ASTM D3763 | 81.3 J |
| Impact strength of cantilever beam gap | Impact strength of cantilever beam gap | ASTM D1822 | 378 kJ/m² |
| Charpy Notched Impact Strength | Charpy Notched Impact Strength -30°C | SK | 无断裂 |
| Charpy Notched Impact Strength | Charpy Notched Impact Strength 23°C | SK | 无断裂 |
| Suspended wall beam without notch impact strength | Suspended wall beam without notch impact strength 23°C | ASTMD256 | 无断裂 |
| flammability | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| Normal combustion performance with a thickness of 1.6mm | Normal combustion performance with a thickness of 1.6mm 1.60mm,UL | ISO 12104 | HB |
| UL flame retardant rating | UL flame retardant rating 3.20mm | ISO 12104 | HB |
| mechanical properties | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| tensile strength | tensile strength Break5 | ASTM D638 | 68.3 Mpa |
| tensile strength | tensile strength Break | ISO 527-2/50 | 68.0 Mpa |
| elongation | elongation Yield5 | ASTM D638 | 6.0 % |
| elongation | elongation Yield | ISO 527-2/50 | 6.0 % |
| elongation | elongation Break5 | ASTM D638 | 150 % |
| elongation | elongation Break | ISO 527-2/50 | 150 % |
| elongation | elongation Break | ISO 527-24 | >50 % |
| Bending modulus | Bending modulus --6 | ASTM D790 | 2410 Mpa |
| Bending modulus | Bending modulus --7,8 | ISO 178 | 2400 Mpa |
| bending strength | bending strength --6 | ASTM D790 | 96.5 Mpa |
| Tensile modulus | Tensile modulus --5 | ASTM D638 | 2210 Mpa |
| Tensile modulus | Tensile modulus -- | ISO 527-2/50 | 2300 Mpa |
| tensile strength | tensile strength Yield5 | ASTM D638 | 62.1 Mpa |
| tensile strength | tensile strength Yield | ISO 527-2/50 | 62.0 Mpa |
| bending strength | bending strength --7,8 | ISO 178 | 98.0 Mpa |
| Wear resistance | Wear resistance | ASTM D1044 | 45 % |
| thermal performance | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| Hot deformation temperature | Hot deformation temperature 0.45MPa,Annealed | ASTM D648 | 139 °C |
| Hot deformation temperature | Hot deformation temperature 0.45MPa | ISO 75-24 | 137 °C |
| Hot deformation temperature | Hot deformation temperature 1.8MPa,Unannealed | ASTM D648 | 122 °C |
| Hot deformation temperature | Hot deformation temperature 1.8MPa,Unannealed | ISO 75-2/A | 120 °C |
| Hot deformation temperature | Hot deformation temperature 1.8MPa,Annealed | ASTM D648 | 136 °C |
| Hot deformation temperature | Hot deformation temperature 1.8MPa | ISO 75-24 | 123 °C |
| Vicat softening temperature | Vicat softening temperature -- | ASTM D152510 | 148 °C |
| Vicat softening temperature | Vicat softening temperature -- | ISO 306/B50 | 143 °C |
| Vicat softening temperature | Vicat softening temperature 50°C/h,B(50N) | ISO 3064 | 143 °C |
| Linear coefficient of thermal expansion | Linear coefficient of thermal expansion MD：-40to82°C | ASTM D696 | 6.8E-05 cm/cm/°C |
| Linear coefficient of thermal expansion | Linear coefficient of thermal expansion MD：-- | ISO 178/1993 | 7E-05 cm/cm/°C |
| Physical properties | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| Melt Volume Flow Rate (MVR) | Melt Volume Flow Rate (MVR) 300°C/1.2kg | ISO 11334 | 12.0 cm3/10min |
| Shrinkage rate | Shrinkage rate MD | ASTM D955 | 0.50-0.70 % |
| Shrinkage rate | Shrinkage rate MD | ISO 294-4 | 0.50-0.70 % |
| Water absorption rate | Water absorption rate 23°C,24hr | ASTMD570 | 0.15 % |
| Water absorption rate | Water absorption rate Equilibrium,23°C,50%RH | ASTMD570 | 0.32 % |
| melt mass-flow rate | melt mass-flow rate 300°C/1.2kg | ASTMD1238 | 15 g/10min |
| Electrical performance | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| Volume resistivity | Volume resistivity -- | ASTM D257 | 2E+17 ohms·cm |
| Volume resistivity | Volume resistivity -- | IEC 600934 | >1.0E+13 ohms·m |
| Dielectric strength | Dielectric strength | ASTMD1494 | 17 KV/mm |
| Dielectric constant | Dielectric constant 60Hz | ASTM D150 | 3.00 |
| Dielectric constant | Dielectric constant 1MHz | ASTMD150 | 3.00 |
| Dielectric constant | Dielectric constant 100Hz | IEC 602504 | 3.00 |
| Dissipation factor | Dissipation factor 50Hz | ASTM D150 | 1E-03 |
| Dissipation factor | Dissipation factor 1MHz | ASTMD150 | 2E-03 |
| Dissipation factor | Dissipation factor 100Hz | IEC 602504 | 1E-03 |
| hardness | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| Rockwell hardness | Rockwell hardness R-Scale | ASTM D785 | 118 |