Unspecified EE168AI Borealis AG

So sánh

Bảng thông số kỹ thuật

impact performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Charpy Notched Impact Strength	Charpy Notched Impact Strength 23°C,Injection	ISO 179/1eA	25 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	Charpy Notched Impact Strength -20°C,Injection	ISO 179/1eA	5.0 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch -20°C,Injection	ISO 179/1eU	110 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch 23°C,Injection	ISO 179/1eU	NoBreak
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap -20°C,Injection	ISO 180/1A	4.0 kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C,Injection	ISO 180/1A	27 kJ/m²
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength -20°C,Injection	ISO 180/1U	72 kJ/m²
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength 23°C,Injection	ISO 180/1U	NoBreak

flammability	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Atomization	Atomization 100°C	DIN 75201	2.5E-04 g

flammability

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Atomization

100°C

DIN 75201

2.5E-04 g

mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Tensile modulus	Tensile modulus Injection	ISO 527-2/1	1700 MPa
tensile strength	tensile strength Yield,Injection	ISO 527-2/50	20.0 MPa
Tensile strain	Tensile strain Yield,Injection	ISO 527-2/50	4.0 %
Bending modulus	Bending modulus Injection	ISO 178	1750 MPa
bending strength	bending strength Injection	ISO 178	30.0 MPa

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
MeltEnergy	MeltEnergy	ISO 11357	64.1 kJ/kg
Hot deformation temperature	Hot deformation temperature 0.45MPa,Unannealed	ISO 75-2/B	97.0 °C
Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed	ISO 75-2/A	54.0 °C
Vicat softening temperature	Vicat softening temperature --	ISO 306/A50	140 °C
Vicat softening temperature	Vicat softening temperature	Vicat softening temperature --	ISO 306/B50	54.0 °C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
density	density	ISO 1183	0.990 g/cm³
melt mass-flow rate	melt mass-flow rate 230°C/2.16kg	ISO 1133	14 g/10min
Shrinkage rate	Shrinkage rate	Internal Method	1.1 %

Physical properties

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

density

ISO 1183

0.990 g/cm³

melt mass-flow rate

230°C/2.16kg

ISO 1133

14 g/10min

Shrinkage rate

Internal Method

1.1 %

Supplementary Information	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Emission	Emission	VDA277	35.0 µgC/g

Supplementary Information

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Emission

VDA277

35.0 µgC/g

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.