PET Comco PETP Comco Nylon GmbH
So sánhBảng thông số kỹ thuật
| impact performance | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| Charpy Notched Impact Strength | Charpy Notched Impact Strength | ISO 179/1eA | 2.0 kJ/m² |
| Impact strength of simply supported beam without notch | Impact strength of simply supported beam without notch | ISO 179/1eU | >50 kJ/m² |
| Impact strength of cantilever beam gap | Impact strength of cantilever beam gap | ISO 180/2A | 2.0 kJ/m² |
| flammability | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| Extreme Oxygen Index | Extreme Oxygen Index | ISO 4589-2 | 25 % |
| UL flame retardant rating | UL flame retardant rating 6.00mm | UL 94 | HB |
| UL flame retardant rating | UL flame retardant rating 3.00mm | UL 94 | HB |
| mechanical properties | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| Tensile creep modulus | Tensile creep modulus 1000hr | ISO 899-1 | 26.0 MPa |
| Tensile strain | Tensile strain Break,23°C | ISO 527-2 | 15 % |
| tensile strength | tensile strength Yield,23°C | ISO 527-2 | 90.0 MPa |
| Tensile modulus | Tensile modulus 23°C | ISO 527-2 | 3700 MPa |
| Compressive stress | Compressive stress 5%Strain | ISO 604 | 103 MPa |
| Compressive stress | Compressive stress 2%Strain | ISO 604 | 51.0 MPa |
| Compressive stress | Compressive stress 1%Strain | ISO 604 | 26.0 MPa |
| thermal performance | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| Maximum operating temperature | Maximum operating temperature inairforshortperiods | 160 °C | |
| Maximum operating temperature | Maximum operating temperature inaircontinuosly | 115 °C | |
| Linear coefficient of thermal expansion | Linear coefficient of thermal expansion MD：ServiceTemperature-Minimum | -20 °C | |
| Linear coefficient of thermal expansion | Linear coefficient of thermal expansion MD：导热系数 | 0.29 W/m/K | |
| Linear coefficient of thermal expansion | Linear coefficient of thermal expansion MD：23to100°C | 8E-05 cm/cm/°C | |
| Linear coefficient of thermal expansion | Linear coefficient of thermal expansion MD：23to60°C | 6E-05 cm/cm/°C | |
| Melting temperature | Melting temperature | 255 °C | |
| Hot deformation temperature | Hot deformation temperature 1.8MPa,Unannealed | ISO 75-2/A | 75.0 °C |
| Physical properties | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| Water absorption rate | Water absorption rate Saturation,23°C | 0.50 % | |
| density | density | ISO 1183 | 1.39 g/cm³ |
| Water absorption rate | Water absorption rate Equilibrium,23°C,50%RH | 0.50 % | |
| Water absorption rate | Water absorption rate after24himmersioninwater:23°C | ISO 62 | 6.0 mg |
| Water absorption rate | Water absorption rate after96himmersioninwater:23°C | ISO 62 | 13.0 mg |
| Electrical performance | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| Compared to the anti leakage trace index | Compared to the anti leakage trace index | IEC 60112 | PLC 0 |
| Dissipation factor | Dissipation factor 1MHz | IEC 60250 | 0.014 |
| Dissipation factor | Dissipation factor 100Hz | IEC 60250 | 1E-03 |
| Relative permittivity | Relative permittivity 1MHz | IEC 60250 | 3.20 |
| Relative permittivity | Relative permittivity 100Hz | IEC 60250 | 3.40 |
| Dielectric strength | Dielectric strength | IEC 60243-1 | 22 kV/mm |
| Volume resistivity | Volume resistivity | IEC 60093 | >1.0E+15 ohms·cm |
| Surface resistivity | Surface resistivity | IEC 60093 | >1.0E+14 ohms |
| hardness | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| Rockwell hardness | Rockwell hardness M-Sale | ISO 2039-2 | 96 |
| Ball Pressure Test | Ball Pressure Test | ISO 2039-1 | 170 MPa |