mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap Izod研磨Notched	ASTM D256	5.9(57.9) kgf-cm/cm(J/m)
bending strength	bending strength 横跨比=16	ASTM D-790	720(71) kgf/cm
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 落锤(15.2×15.2×0.3cm重1.4kg半径0.64cm)	ASTM D256	136(14) kg-cm(J)
tensile strength	tensile strength 初级Strain速率0.1cm/cm/min	ASTM D-638	390(38) kgf/cm
Bending modulus	Bending modulus	ASTM D-790	19000 kgf/cm

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Vicat softening temperature	Vicat softening temperature 50℃/hr,5kg	ASTM D-1525，未退火	86 ℃
Hot deformation temperature	Hot deformation temperature 2℃/min,18.6kgf/cm，Annealed	ASTM D-648	79 ℃
Vicat softening temperature	Vicat softening temperature 50℃/hr,1kg	ASTM D-1525，未退火	98 ℃
Temperature range for use	Temperature range for use 与残余应力大小有关		71-82 ℃

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
density	density	ASTM D-792	1.15
Refractive index	Refractive index	ASTM D-542	1.49
Transmittance rate	Transmittance rate	ASTM D-1003	91 %
Rockwell hardness	Rockwell hardness	ASTM D-758（M级）	45
Shrinkage rate	Shrinkage rate (冷模/冷件),48hrs	ASTM D-935	0.3-0.8 %

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.