PA66 Durethan® AKV30H2.0 BK LANXESS GERMANY

Đặc tính:
Đóng gói: LANXESS LANXESS
So sánh
Xem giá

Bảng thông số kỹ thuật

impact performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength -30°C	ISO 180/1U	55 kJ/m²
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength 23°C	ISO 180/1U	60 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch 23°C	ISO 179/1eU	75 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch -30°C	ISO 179/1eU	60 kJ/m²

flammability	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
UL flame retardant rating	UL flame retardant rating 0.75mm	UL 94	HB
	UL flame retardant rating	UL flame retardant rating 1.5mm	UL 94	HB
		UL flame retardant rating	UL flame retardant rating 1.6mm	UL 94	HB
			UL flame retardant rating	UL flame retardant rating 3.0mm	UL 94	HB
			UL flame retardant rating	UL flame retardant rating	UL flame retardant rating 3.2mm	UL 94	HB
Burning wire flammability index	Burning wire flammability index 0.8mm	IEC 60695-2-12	700 °C
	Burning wire flammability index	Burning wire flammability index 1.6mm	IEC 60695-2-12	700 °C
	Burning wire flammability index	Burning wire flammability index	Burning wire flammability index 3.0mm	IEC 60695-2-12	700 °C
Extreme Oxygen Index	Extreme Oxygen Index	ISO 4589-2	23 %
BurningBehavior	BurningBehavior >1.00mm	ISO 3795	passed

mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
bending strength	bending strength FlexuralStrainatFlexuralStrength6(23°C)		4.0 %
	bending strength	bending strength 23°C	ISO 178	270 Mpa
		bending strength	bending strength 3.5%Strain	ISO 178/A	265 Mpa
		bending strength	bending strength	bending strength 23°C	ASTM D790	270 Mpa
Tensile modulus	Tensile modulus 23°C	ASTM D638	9170 Mpa
Tensile modulus	Tensile modulus	Tensile modulus 23°C	ISO 527-2/1	10000 Mpa
tensile strength	tensile strength Break,23°C	ASTM D638	170 Mpa
tensile strength	tensile strength	tensile strength Break,23°C	ISO 527-2/5	175 Mpa
Bending modulus	Bending modulus 23°C	ASTM D790	8690 Mpa
Bending modulus	Bending modulus	Bending modulus 23°C	ISO 178/A	9200 Mpa
elongation	elongation Break,23°C	ASTM D638	3.0 %
Tensile strain	Tensile strain Break,23°C	ISO 527-2/5	3.0 %
Nominal tensile fracture strain	Nominal tensile fracture strain 23°C	ISO 527-2/50	4.4 %

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Melting temperature	Melting temperature	ISO 11357-3	263 °C
Ball Pressure Test	Ball Pressure Test 253°C	IEC 60695-10-2	Pass
Vicat softening temperature	Vicat softening temperature --	ISO 306/B120	>230 °C
Vicat softening temperature	Vicat softening temperature	Vicat softening temperature --	ISO 306/B50	230 °C
Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed	ISO 75-2/A	>240 °C
	Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed,4.00mm	ASTM D648	>249 °C
		Hot deformation temperature	Hot deformation temperature 0.45MPa,Unannealed	ISO 75-2/B	250 °C
		Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 0.45MPa,Unannealed,4.00mm	ASTM D648	>249 °C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion MD：23to55°C	ISO 11359-2	3E-05 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion TD：23to55°C	ISO 11359-2	9E-05 cm/cm/°C
RTI Elec	RTI Elec 0.75mm	UL 746	125 °C
RTI Elec	RTI Elec	RTI Elec 1.5mm	UL 746	125 °C
RTI Imp	RTI Imp 0.75mm	UL 746	90.0 °C
RTI Imp	RTI Imp	RTI Imp 1.5mm	UL 746	105 °C
RTI Str	RTI Str 0.75mm	UL 746	110 °C
RTI Str	RTI Str	RTI Str 1.5mm	UL 746	115 °C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Water absorption rate	Water absorption rate Saturation,23°C	ISO 62	5.5 %
Shrinkage rate	Shrinkage rate MD:120°C,2hr,2.00mm3	ISO 294-4	0.070 %
	Shrinkage rate	Shrinkage rate MD:290°C,2.00mm2	ISO 294-4	0.39 %
		Shrinkage rate	Shrinkage rate TD:120°C,2hr,2.00mm3	ISO 294-4	0.13 %
		Shrinkage rate	Shrinkage rate	Shrinkage rate TD:290°C,2.00mm2	ISO 294-4	0.93 %
Apparent density	Apparent density	ISO 60	0.70 g/cm³
Water absorption rate	Water absorption rate Equilibrium,23°C,50%RH	ISO 62	2.0 %

Electrical performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Surface resistivity	Surface resistivity	IEC 60093	1E+15 ohms
Relative permittivity	Relative permittivity 23°C,100Hz	IEC 60250	4.00
Relative permittivity	Relative permittivity	Relative permittivity 23°C,1MHz	IEC 60250	4.00
Dissipation factor	Dissipation factor 23°C,50Hz	IEC 60250	0.012
Volume resistivity	Volume resistivity 23°C	IEC 60093	1E+15 ohms·cm
Dielectric strength	Dielectric strength 23°C,1.00mm	IEC 60243-1	35 KV/mm
Dielectric strength	Dielectric strength	Dielectric strength 23°C,3.00mm	IEC 60243-1	30 KV/mm
Dielectric constant	Dielectric constant 23°C,50Hz	IEC 60250	4.00
Dielectric constant	Dielectric constant	Dielectric constant 23°C,1MHz	IEC 60250	4.00
Dissipation factor	Dissipation factor 23°C,100Hz	IEC 60250	0.012
Dissipation factor	Dissipation factor	Dissipation factor 23°C,1MHz	IEC 60250	0.0190.019
Compared to the anti leakage trace index	Compared to the anti leakage trace index SolutionA	IEC 60112	V

hardness	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Ball Pressure Test	Ball Pressure Test	ISO 2039-1	220 Mpa

hardness

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Ball Pressure Test

ISO 2039-1

220 Mpa

film	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Thin film puncture strength	Thin film puncture strength --8	ISO 6603-2	800 N
	Thin film puncture strength	Thin film puncture strength --7	ISO 6603-2	900 N
		Thin film puncture strength	Thin film puncture strength --8	ISO 6603-2	2.30 J
		Thin film puncture strength	Thin film puncture strength	Thin film puncture strength --7	ISO 6603-2	2.80 J

Supplementary Information	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
ISO Shortcut	ISO Shortcut	ISO 1874	PA66.GHR.14-100.GF30

Supplementary Information

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

ISO Shortcut

ISO 1874

PA66.GHR.14-100.GF30

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.