ABS Sindustris ABS LAF423T Sincerity Australia Pty Ltd.

So sánh

Bảng thông số kỹ thuật

impact performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap -30°C,3.20mm	ASTM D256	78 J/m
	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap -30°C,6.40mm	ASTM D256	78 J/m
		Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C,3.20mm	ASTM D256	270 J/m
		Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C,6.40mm	ASTM D256	230 J/m

flammability	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
UL flame retardant rating	UL flame retardant rating 1.5mm	UL 94	V-0
	UL flame retardant rating	UL flame retardant rating 2.0mm	UL 94	V-0
		UL flame retardant rating	UL flame retardant rating 2.5mm	UL 94	V-0
		UL flame retardant rating	UL flame retardant rating	UL flame retardant rating 3.0mm	UL 94	V-0

mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
elongation	elongation Break,3.20mm	ASTM D638	25 %
Bending modulus	Bending modulus 6.40mm	ASTM D790	2600 MPa
bending strength	bending strength 6.40mm	ASTM D790	68.6 MPa
Tensile modulus	Tensile modulus 3.20mm	ASTM D638	2160 MPa
tensile strength	tensile strength Yield,3.20mm	ASTM D638	42.2 MPa
elongation	elongation Yield,3.20mm	ASTM D638	5.0 %

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
RTI	RTI	UL 746	75.0 °C
Hot deformation temperature	Hot deformation temperature 0.45MPa,Unannealed,6.40mm	ASTM D648	84.0 °C
Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed,6.40mm	ASTM D648	76.0 °C
Vicat softening temperature	Vicat softening temperature	ASTM D15255	84.0 °C
RTI Elec	RTI Elec	UL 746	85.0 °C
RTI Imp	RTI Imp	UL 746	75.0 °C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
density	density	ASTM D792	1.18 g/cm³
melt mass-flow rate	melt mass-flow rate 220°C/10.0kg	ASTM D1238	52 g/10min
Shrinkage rate	Shrinkage rate MD：3.20mm	ASTM D955	0.40to0.70 %

Physical properties

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

density

ASTM D792

1.18 g/cm³

melt mass-flow rate

220°C/10.0kg

ASTM D1238

52 g/10min

Shrinkage rate

MD：3.20mm

ASTM D955

0.40to0.70 %

hardness	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Rockwell hardness	Rockwell hardness R-Scale	ASTM D785	104

hardness

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Rockwell hardness

R-Scale

ASTM D785

104

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.