PBT/PET Pocan® ECOT3230 LANXESS GERMANY

So sánh
Xem giá

Bảng thông số kỹ thuật

impact performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength 23℃23°C	ISO 180/1U	55 kJ/m²
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength -30℃-30°C	ISO 180/1U	55 kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23℃23°C	ISO 180-1A	< 10 kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap -30℃-30°C	ISO 180-1A	< 10 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch 23℃23°C	ISO 179/1eU	65 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch -30℃-30°C	ISO 179/1eU	55 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength 23℃23°C	ISO 179/1eA	< 10 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	Charpy Notched Impact Strength -30℃-30°C	ISO 179/1eA	< 10 kJ/m²

mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Bending strain	Bending strain		3 %
bending strength	bending strength 23℃23℃4	ISO 178	230 Mpa
Bending modulus	Bending modulus 23℃23℃4	ISO 178-A	10300 Mpa
Tensile strain	Tensile strain Break，23℃Break，23℃	ISO 527-2/5	2.8 %
tensile strength	tensile strength Break，23℃Break，23℃	ISO 527-2/5	145 Mpa
Tensile modulus	Tensile modulus 23℃23℃	ISO 527-1-2	10400 Mpa

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Melting temperature	Melting temperature	ISO 11357-3	225 to 250 °C
Vicat softening temperature	Vicat softening temperature B120B120	ISO 306/B120	205 °C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion TD：23~55℃TD：23 to 55℃	ISO 11359-2	0.000090 1/℃
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion MD：23~55℃MD：23 to 55℃	ISO 11359-2	0.000030 1/℃

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Water absorption rate	Water absorption rate Equilibrium，23℃，50% RHEquilibrium，23℃，50% RH	ISO 62	0.1 %
Water absorption rate	Water absorption rate	Water absorption rate Saturation，23℃Saturation，23℃	ISO 62	0.3 %
Shrinkage rate	Shrinkage rate MD：120℃，2.0 mm，2 hrsFlow : 120°C, 2 hr, 2.00 mm 33	ISO 294-4	0.1 %
	Shrinkage rate	Shrinkage rate MD：270℃，2.0 mmFlow : 518°F, 0.0787 in 22	ISO 294-4	0.3 %
		Shrinkage rate	Shrinkage rate TD：120℃，2.0 mm，2 hrsAcross Flow : 120°C, 2 hr, 2.00 mm 33	ISO 294-4	0.2 %
		Shrinkage rate	Shrinkage rate	Shrinkage rate TD：270℃，2.0 mmAcross Flow : 518°F, 0.0787 in 22	ISO 294-4	0.9 %
Melt Volume Flow Rate (MVR)	Melt Volume Flow Rate (MVR) 260℃，5 kg260℃/5.0 kg	ISO 1133	30 cm3/10min
Apparent density	Apparent density	ISO 60	0.8 g/cm³
density	density 23°C	ISO 1183	1.55 g/cm³

Electrical performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Compared to the anti leakage trace index	Compared to the anti leakage trace index Solution ASolution A	IEC 60112	PLC 2

Electrical performance

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Compared to the anti leakage trace index

Solution ASolution A

IEC 60112

PLC 2

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.