flammability	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
UL flame retardant rating	UL flame retardant rating 1.5mm	UL 94	HB
UL flame retardant rating	UL flame retardant rating 3.0mm	UL 94	HB
UL flame retardant rating	UL flame retardant rating 6.0mm	UL 94	HB

flammability

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

UL flame retardant rating

1.5mm

UL 94

UL flame retardant rating

3.0mm

UL 94

UL flame retardant rating

6.0mm

UL 94

mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
tensile strength	tensile strength Break,23°C	ASTM D638	175 Mpa
bending strength	bending strength 23°C	ASTM D790	265 Mpa
Bending modulus	Bending modulus 23°C	ISO 178	8400 Mpa
Bending modulus	Bending modulus	Bending modulus 23°C	ASTM D790	9380 Mpa
Tensile strain	Tensile strain Break,23°C	ISO 527-2	3.0 %
elongation	elongation Break,23°C	ASTM D638	3.0 %
tensile strength	tensile strength Break,23°C	ISO 527-2	175 Mpa

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
RTI Elec	RTI Elec 3.0mm	UL 746	140 °C
RTI Elec	RTI Elec	RTI Elec 1.5mm	UL 746	140 °C
Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed	ISO 75-2/A	54.0 °C
	Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed	ASTM D648	208 °C
	Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 0.45MPa,Unannealed	ISO 75-2/B	174 °C
RTI Elec	RTI Elec 0.71mm	UL 746	130 °C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion MD	ASTME831	3.8E-05 cm/cm/°C
Melting temperature	Melting temperature	ISO 3146	220 °C
Melting temperature	Melting temperature	Melting temperature	ASTM D3418	220 °C
RTI Elec	RTI Elec 6.0mm	UL 746	140 °C
RTI Imp	RTI Imp 0.71mm	UL 746	115 °C
	RTI Imp	RTI Imp 1.5mm	UL 746	115 °C
		RTI Imp	RTI Imp 3.0mm	UL 746	120 °C
		RTI Imp	RTI Imp	RTI Imp 6.0mm	UL 746	120 °C
RTI Str	RTI Str 0.71mm	UL 746	140 °C
	RTI Str	RTI Str 1.5mm	UL 746	140 °C
		RTI Str	RTI Str 3.0mm	UL 746	140 °C
		RTI Str	RTI Str	RTI Str 6.0mm	UL 746	140 °C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Water absorption rate	Water absorption rate Equilibrium,23°C,50%RH	ISO 62	1.8 %
	Water absorption rate	Water absorption rate Equilibrium,50%RH	ASTM D570	1.8 %
		Water absorption rate	Water absorption rate Saturation,23°C	ISO 62	6.4 %
			Water absorption rate	Water absorption rate Saturation	ASTM D570	6.4 %
				Water absorption rate	Water absorption rate 23°C,24hr	ISO 62	1.1 %
				Water absorption rate	Water absorption rate	Water absorption rate 24hr	ASTM D570	1.1 %
Shrinkage rate	Shrinkage rate MD：3.18mm		0.30 %

Electrical performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Volume resistivity	Volume resistivity	IEC 60093	>1.0E+13 ohms·cm
Dielectric strength	Dielectric strength 1.50mm	ASTM D149	22 KV/mm
Volume resistivity	Volume resistivity 1.50mm	ASTM D257	>1.0E+13 ohms·cm

Electrical performance

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Volume resistivity

IEC 60093

>1.0E+13 ohms·cm

Dielectric strength

1.50mm

ASTM D149

22 KV/mm

Volume resistivity

1.50mm

ASTM D257

>1.0E+13 ohms·cm

hardness	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Rockwell hardness	Rockwell hardness R-Scale	ASTM D785	120

hardness

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Rockwell hardness

R-Scale

ASTM D785

120

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.