| impact performance | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| Impact strength of cantilever beam gap | Impact strength of cantilever beam gap 3.17mm | ASTM D256 | 590 J/m |
| flammability | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| UL flame retardant rating | UL flame retardant rating 2.5mm | UL 94 | 5VA |
| UL flame retardant rating | UL flame retardant rating 3.0mm | UL 94 | 5VA |
| Burning wire flammability index | Burning wire flammability index 1.5mm | IEC 60695-2-12 | 925 °C |
| Burning wire flammability index | Burning wire flammability index 2.0mm | IEC 60695-2-12 | 925 °C |
| Burning wire flammability index | Burning wire flammability index 3.0mm | IEC 60695-2-12 | 950 °C |
| Hot filament ignition temperature | Hot filament ignition temperature 1.5mm | IEC 60695-2-13 | 700 °C |
| Hot filament ignition temperature | Hot filament ignition temperature 2.0mm | IEC 60695-2-13 | 700 °C |
| Hot filament ignition temperature | Hot filament ignition temperature 3.0mm | IEC 60695-2-13 | 700 °C |
| UL flame retardant rating | UL flame retardant rating 1.5mm | UL 94 | V-0 |
| UL flame retardant rating | UL flame retardant rating 2.0mm | UL 94 | 5VB |
| mechanical properties | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| tensile strength | tensile strength Yield,3.17mm | ASTM D638 | 60.0 MPa |
| elongation | elongation Break,3.17mm | ASTM D638 | 65 % |
| Bending modulus | Bending modulus 3.17mm | ASTM D790 | 2690 MPa |
| bending strength | bending strength Yield,3.17mm | ASTM D790 | 88.9 MPa |
| thermal performance | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| Hot deformation temperature | Hot deformation temperature 1.8MPa,Unannealed | ASTM D648 | 85.0 °C |
| RTI Elec | RTI Elec | UL 746 | 60.0 °C |
| RTI Imp | RTI Imp | UL 746 | 60.0 °C |
| RTI | RTI | UL 746 | 60.0 °C |
| Physical properties | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| density | density | ASTM D792 | 1.17 g/cm³ |
| melt mass-flow rate | melt mass-flow rate 230°C/3.8kg | ASTM D1238 | 12 g/10min |
| melt mass-flow rate | melt mass-flow rate 260°C/2.16kg | ASTM D1238 | 16 g/10min |
| Shrinkage rate | Shrinkage rate MD | ASTM D955 | 0.40to0.60 % |
| Electrical performance | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| Hot wire ignition | Hot wire ignition 3.0mm | UL 746 | PLC 2 |
| Dielectric strength | Dielectric strength | ASTM D149 | 18 kV/mm |
| Compared to the anti leakage trace index | Compared to the anti leakage trace index CTI | UL 746 | PLC 0 |
| Compared to the anti leakage trace index | Compared to the anti leakage trace index CTI | UL 746 | PLC 0 |
| High arc combustion index | High arc combustion index 1.50mm | UL 746 | PLC 0 |
| High arc combustion index | High arc combustion index 2.50mm | UL 746 | PLC 0 |
| High arc combustion index | High arc combustion index 3.00mm | UL 746 | PLC 0 |
| High arc combustion index | High arc combustion index 1.5mm | UL 746 | PLC 1 |
| High arc combustion index | High arc combustion index 2.5mm | UL 746 | PLC 1 |
| High arc combustion index | High arc combustion index 3.0mm | UL 746 | PLC 1 |
| High voltage arc tracing rate | High voltage arc tracing rate HVTR | UL 746 | PLC 4 mm/min |
| High voltage arc tracing rate | High voltage arc tracing rate HVTR | UL 746 | PLC 3 |
| Hot wire ignition | Hot wire ignition 1.50mm | UL 746 | PLC 2 sec |
| Hot wire ignition | Hot wire ignition 2.50mm | UL 746 | PLC 2 sec |
| Hot wire ignition | Hot wire ignition 3.00mm | UL 746 | PLC 1 sec |
| Hot wire ignition | Hot wire ignition 1.5mm | UL 746 | PLC 3 |
| Hot wire ignition | Hot wire ignition 2.5mm | UL 746 | PLC 3 |