PA6 Ultraflow K-FHG6 DSM Additive Manufacturing

So sánh

Bảng thông số kỹ thuật

impact performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Charpy Notched Impact Strength	Charpy Notched Impact Strength -30°C	ISO 179/1eA	10 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	Charpy Notched Impact Strength 23°C	ISO 179/1eA	14 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch -30°C	ISO 179/1eU	65 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch 23°C	ISO 179/1eU	85 kJ/m²

flammability	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
UL flame retardant rating	UL flame retardant rating 1.6mm	IEC 60695-11-10,-20	HB

flammability

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

UL flame retardant rating

1.6mm

IEC 60695-11-10,-20

mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Tensile modulus	Tensile modulus	ISO 527-2	9350 MPa
tensile strength	tensile strength Break	ISO 527-2	160 MPa
Tensile strain	Tensile strain Break	ISO 527-2	3.0 %
Bending modulus	Bending modulus	ISO 178	8500 MPa
bending strength	bending strength	ISO 178	235 MPa

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Melting temperature	Melting temperature	ISO 11357-3	220 °C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion MD	ISO 11359-2	2E-05 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion TD	ISO 11359-2	7E-05 cm/cm/°C
Hot deformation temperature	Hot deformation temperature 0.45MPa,Unannealed	ISO 75-2/B	220 °C
Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed	ISO 75-2/A	200 °C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Water absorption rate	Water absorption rate Saturation,23°C	ISO 62	6.0 %
Water absorption rate	Water absorption rate	Water absorption rate Equilibrium,23°C,50%RH	ISO 62	1.8 %
Shrinkage rate	Shrinkage rate TD	ISO 294-4	1.1 %
Shrinkage rate	Shrinkage rate	Shrinkage rate MD	ISO 294-4	0.30 %
density	density	ISO 1183	1.35 g/cm³

Electrical performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Surface resistivity	Surface resistivity	IEC 60093	-- ohms
Volume resistivity	Volume resistivity	IEC 60093	>1.0E+15 ohms·cm
Relative permittivity	Relative permittivity 100Hz	IEC 60250	3.50
Relative permittivity	Relative permittivity	Relative permittivity 1MHz	IEC 60250	3.30
Dissipation factor	Dissipation factor 100Hz	IEC 60250	5E-03
Dissipation factor	Dissipation factor	Dissipation factor 1MHz	IEC 60250	0.015

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.