impact performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch -30°C	ISO 179/1eU	40 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch 23°C	ISO 179/1eU	60 kJ/m²

impact performance

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Impact strength of simply supported beam without notch

-30°C

ISO 179/1eU

40 kJ/m²

Impact strength of simply supported beam without notch

23°C

ISO 179/1eU

60 kJ/m²

flammability	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Burning rate	Burning rate 1.00mm	ISO 3795	<100 mm/min
UL flame retardant rating	UL flame retardant rating 0.75mm	UL 94	HB
	UL flame retardant rating	UL flame retardant rating 1.5mm	UL 94	HB
		UL flame retardant rating	UL flame retardant rating 0.75mm	IEC 60695-11-10,-20	HB
		UL flame retardant rating	UL flame retardant rating	UL flame retardant rating 1.5mm	IEC 60695-11-10,-20	HB
Extreme Oxygen Index	Extreme Oxygen Index	ISO 4589-2	20 %
FMVSS flammability	FMVSS flammability	FMVSS302	B
Fogging-G-value	Fogging-G-value condensate	ISO 6452	0.0 g

mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Bending modulus	Bending modulus	ASTM D790/ISO 178	13500 kg/cm²(MPa)[Lb/in²]
Rockwell hardness	Rockwell hardness	ASTM D785	100
Tensile modulus	Tensile modulus	ASTM D412/ISO 527	15500 kg/cm²(MPa)[Lb/in²]
Tensile modulus	Tensile modulus	Tensile modulus	ISO 527-2	15500 Mpa
tensile strength	tensile strength Break	ISO 527-2	182 Mpa
Tensile strain	Tensile strain Break	ISO 527-2	2.0 %
Tensile creep modulus	Tensile creep modulus 1hr	ISO 899-1	15600 Mpa
Tensile creep modulus	Tensile creep modulus	Tensile creep modulus 1000hr	ISO 899-1	13300 Mpa
Bending modulus	Bending modulus	ISO 178	13500 Mpa

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Effective thermal diffusivity coefficient	Effective thermal diffusivity coefficient		1.4E-07 m²/s
Hot deformation temperature	Hot deformation temperature HDT	ASTM D648/ISO 75	226 ℃（℉）
Hot deformation temperature	Hot deformation temperature	Hot deformation temperature HDT	ASTM D648/ISO 75	250 ℃（℉）
Combustibility (rate)	Combustibility (rate)	UL 94	HB
Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed	ISO 75-2/A	226 °C
Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 8.0MPa,Unannealed	ISO 75-2/C	180 °C
Vicat softening temperature	Vicat softening temperature	ISO 306/B50	230 °C
Melting temperature	Melting temperature	ISO 11357-3	252 °C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion MD	ISO 11359-2	1.5E-05 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion TD	ISO 11359-2	8.3E-05 cm/cm/°C
thermal conductivity	thermal conductivity		0.32 W/m/K

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Water absorption rate	Water absorption rate	ASTM D570/ISO 62	0.14 %
Shrinkage rate	Shrinkage rate	ASTM D955	0.85 %
density	density	ASTM D792/ISO 1183	1690
Top out temperature	Top out temperature		170 °C
Shrinkage rate	Shrinkage rate TD	ISO 294-4	0.80 %
Shrinkage rate	Shrinkage rate	Shrinkage rate MD	ISO 294-4	0.20 %
Melt Volume Flow Rate (MVR)	Melt Volume Flow Rate (MVR) 280°C/2.16kg	ISO 1133	2.50 cm3/10min
Water absorption rate	Water absorption rate Saturation,23°C,2.00mm	ISO 62	0.62 %
Water absorption rate	Water absorption rate	Water absorption rate Equilibrium,23°C,2.00mm,50%RH	ISO 62	0.14 %

Electrical performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Compared to the anti leakage trace index	Compared to the anti leakage trace index	IEC 60112	PLC 2
Compared to the anti leakage trace index	Compared to the anti leakage trace index	Compared to the anti leakage trace index CTI	UL 746	PLC 2
Dissipation factor	Dissipation factor 1MHz	IEC 60250	0.011
Dissipation factor	Dissipation factor	Dissipation factor 100Hz	IEC 60250	7E-03
Relative permittivity	Relative permittivity 1MHz	IEC 60250	4.40
Relative permittivity	Relative permittivity	Relative permittivity 100Hz	IEC 60250	4.50
Dielectric strength	Dielectric strength	IEC 60243-1	32 KV/mm
Volume resistivity	Volume resistivity	IEC 60093	1E+15 ohms·cm
Surface resistivity	Surface resistivity	IEC 60093	1E+14 ohms
Volume resistivity	Volume resistivity	ASTM D257/IEC 60093	1.00E+13 Ω.cm
Dielectric constant	Dielectric constant	ASTM D150/IEC 60250	4.4
Dielectric constant	Dielectric constant	Dielectric constant	ASTM D150/IEC 60250	4.5
Surface resistivity	Surface resistivity	ASTM D257/IEC 60093	1.00E+14 Ω

hardness	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Rockwell hardness	Rockwell hardness M-Sale	ISO 2039-2	100
Rockwell hardness	Rockwell hardness R-Sale	ISO 2039-2	120

hardness

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Rockwell hardness

M-Sale

ISO 2039-2

100

Rockwell hardness

R-Sale

ISO 2039-2

120

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.