PC WONDERLOY® PC-385 CHI MEI CORPORATION
So sánhBảng thông số kỹ thuật
| impact performance | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| Charpy Notched Impact Strength | Charpy Notched Impact Strength -30°C | ISO 179 | 45 kJ/m² |
| Charpy Notched Impact Strength | Charpy Notched Impact Strength 23°C | ISO 179 | 55 kJ/m² |
| Impact strength of cantilever beam gap | Impact strength of cantilever beam gap -30°C,3.18mm | ASTM D256 | 490 J/m |
| Impact strength of cantilever beam gap | Impact strength of cantilever beam gap 23°C,3.18mm | ASTM D256 | 590 J/m |
| Impact strength of cantilever beam gap | Impact strength of cantilever beam gap -30°C | ISO 180 | 45 kJ/m² |
| Impact strength of cantilever beam gap | Impact strength of cantilever beam gap 23°C | ISO 180 | 55 kJ/m² |
| flammability | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| UL flame retardant rating | UL flame retardant rating 1.5mm | UL 94 | HB |
| mechanical properties | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| tensile strength | tensile strength Break | ISO 527-2/50 | 57.0 MPa |
| Tensile strain | Tensile strain Break,23°C | ASTM D638 | 90 % |
| Tensile strain | Tensile strain Break | ISO 527-2/50 | 130 % |
| Bending modulus | Bending modulus 23°C | ASTM D790 | 2300 MPa |
| Bending modulus | Bending modulus | ISO 178 | 2300 MPa |
| bending strength | bending strength 23°C | ASTM D790 | 78.5 MPa |
| bending strength | bending strength | ISO 178 | 85.0 MPa |
| tensile strength | tensile strength Yield,23°C | ASTM D638 | 53.0 MPa |
| tensile strength | tensile strength Yield | ISO 527-2/50 | 55.0 MPa |
| thermal performance | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| Vicat softening temperature | Vicat softening temperature -- | ASTM D152510 | 140 °C |
| Vicat softening temperature | Vicat softening temperature -- | ASTM D152511 | 133 °C |
| Vicat softening temperature | Vicat softening temperature -- | ISO 306/A50 | 140 °C |
| Vicat softening temperature | Vicat softening temperature -- | ISO 306/B50 | 125 °C |
| Linear coefficient of thermal expansion | Linear coefficient of thermal expansion MD：-40to40°C | ASTME831 | 7.5E-05 cm/cm/°C |
| Linear coefficient of thermal expansion | Linear coefficient of thermal expansion MD：23to55°C | ISO 11359-2 | 7.5E-05 cm/cm/°C |
| Hot deformation temperature | Hot deformation temperature 1.8MPa,Unannealed,3.20mm | ASTM D648 | 110 °C |
| Hot deformation temperature | Hot deformation temperature 1.8MPa,Unannealed,6.40mm | ASTM D648 | 118 °C |
| Hot deformation temperature | Hot deformation temperature 1.8MPa,Unannealed,4.00mm | ISO 75-2/A | 108 °C |
| Physical properties | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| density | density | ASTM D792 | 1.15 g/cm³ |
| density | density 23°C | ISO 1183 | 1.15 g/cm³ |
| melt mass-flow rate | melt mass-flow rate 260°C/5.0kg | ASTM D1238 | 20 g/10min |
| melt mass-flow rate | melt mass-flow rate 260°C/5.0kg | ISO 1133 | 20 g/10min |
| Spiral flow length | Spiral flow length | Internal Method | 28.0 cm |
| Shrinkage rate | Shrinkage rate MD | ASTM D955 | 0.40to0.60 % |
| Shrinkage rate | Shrinkage rate | ISO 2577 | 0.40to0.60 % |
| Electrical performance | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| Surface resistivity | Surface resistivity | IEC 60093 | 1E+16 ohms |
| Volume resistivity | Volume resistivity | IEC 60093 | 1E+18 ohms·cm |
| Dielectric constant | Dielectric constant 1MHz | IEC 60250 | 3.00 |
| hardness | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| Rockwell hardness | Rockwell hardness R-Sale,23°C | ASTM D785 | 114 |
| Rockwell hardness | Rockwell hardness R-Sale,23°C | ISO 2039-2 | 114 |