TPC-ET Hytrel® 6359FG NC010 DUPONT USA
So sánhBảng thông số kỹ thuật
| impact performance | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| Charpy Notched Impact Strength | Charpy Notched Impact Strength -40°C | ISO 179/1eA | 15 kJ/m² |
| Charpy Notched Impact Strength | Charpy Notched Impact Strength -30°C | ISO 179/1eA | 25 kJ/m² |
| Charpy Notched Impact Strength | Charpy Notched Impact Strength 23°C,Partial Break | ISO 179/1eA | 110 kJ/m² |
| Impact strength of simply supported beam without notch | Impact strength of simply supported beam without notch 23°C | ISO 179/1eU | NoBreak |
| Impact strength of cantilever beam gap | Impact strength of cantilever beam gap -40°C | ISO 180/1A | 19 kJ/m² |
| Impact strength of cantilever beam gap | Impact strength of cantilever beam gap 23°C | ISO 180/1A | 81 kJ/m² |
| flammability | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| Burning rate | Burning rate 1.00mm | ISO 3795 | <100 mm/min |
| FMVSS flammability | FMVSS flammability | FMVSS302 | B |
| Fogging-G-value | Fogging-G-value condensate | ISO 6452 | 1E-04 g |
| elastomer | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| tear strength | tear strength 横向Flow | ISO 34-1 | 150 kN/m |
| tear strength | tear strength Flow | ISO 34-1 | 160 kN/m |
| mechanical properties | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| Tensile modulus | Tensile modulus | ISO 527-2 | 260 MPa |
| tensile strength | tensile strength Yield | ISO 527-2 | 19.0 MPa |
| tensile strength | tensile strength Break | ISO 527-2 | 41.0 MPa |
| tensile strength | tensile strength 5.0%Strain | ISO 527-2 | 12.0 MPa |
| tensile strength | tensile strength 10%Strain | ISO 527-2 | 15.0 MPa |
| Tensile strain | Tensile strain Yield | ISO 527-2 | 27 % |
| Tensile strain | Tensile strain Break | ISO 527-2 | >300 % |
| thermal performance | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| Hot deformation temperature | Hot deformation temperature 0.45MPa,Unannealed | ISO 75-2/B | 85.0 °C |
| Hot deformation temperature | Hot deformation temperature 1.8MPa,Unannealed | ISO 75-2/A | 45.0 °C |
| Brittle temperature | Brittle temperature | ISO 974 | -100 °C |
| Vicat softening temperature | Vicat softening temperature -- | ISO 306/A50 | 195 °C |
| Vicat softening temperature | Vicat softening temperature -- | ISO 306/B50 | 100 °C |
| Melting temperature | Melting temperature | ISO 11357-3 | 211 °C |
| Effective thermal diffusivity coefficient | Effective thermal diffusivity coefficient | 5.44E-08 m²/s |
| Physical properties | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| Water absorption rate | Water absorption rate Equilibrium,23°C,2.00mm,50%RH | ISO 62 | 0.20 % |
| ThermalConductivityofMelt | ThermalConductivityofMelt | 0.14 W/m/K | |
| density | density | ISO 1183 | 1.22 g/cm³ |
| melt mass-flow rate | melt mass-flow rate 230°C/2.16kg | ISO 1133 | 9.0 g/10min |
| Melt Volume Flow Rate (MVR) | Melt Volume Flow Rate (MVR) 230°C/2.16kg | ISO 1133 | 8.50 cm³/10min |
| Shrinkage rate | Shrinkage rate TD | ISO 294-4 | 1.5 % |
| Shrinkage rate | Shrinkage rate MD | ISO 294-4 | 1.5 % |
| Water absorption rate | Water absorption rate Saturation,23°C,2.00mm | ISO 62 | 0.60 % |
| MediumDensity | MediumDensity | 1.04 g/cm³ | |
| SpecificHeatCapacity of Melt | SpecificHeatCapacity of Melt | 2160 J/kg/°C |
| Electrical performance | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| Compared to the anti leakage trace index | Compared to the anti leakage trace index | IEC 60112 | PLC 0 |
| hardness | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| Shore hardness | Shore hardness ShoreD | ISO 868 | 63 |
| Shore hardness | Shore hardness ShoreD,15Sec | ISO 868 | 58 |
| Supplementary Information | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| Odor | Odor | VDA270 | 2.50 |