impact performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Charpy Notched Impact Strength	Charpy Notched Impact Strength 23°C	ISO 179/1eA2	90.0 kJ/m²
	Charpy Notched Impact Strength	Charpy Notched Impact Strength -30°C	ISO 179/1eA2	13.0 kJ/m²
		Charpy Notched Impact Strength	Charpy Notched Impact Strength 23°C	ISO 179/1eU2	NoBreak
		Charpy Notched Impact Strength	Charpy Notched Impact Strength	Charpy Notched Impact Strength -30°C	ISO 179/1eU2	NoBreak
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C	ISO 180/4A	88 kJ/m²
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength 23°C	ISO 180	NoBreak

flammability	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Limiting Oxygen Index (LOI)	Limiting Oxygen Index (LOI)	ISO 4589-22	26 %
Burning Behav.atthicknessh	Burning Behav.atthicknessh 3.20mm,UL	ISO 12102	HB
Burning Behav.	Burning Behav. 1.60mm,UL	ISO 12102	HB
UL flame retardant rating	UL flame retardant rating 1.6mm	UL 94	HB
UL flame retardant rating	UL flame retardant rating	UL flame retardant rating 3.2mm	UL 94	HB

mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Tensile strain	Tensile strain Break	ISO 527-2/50	150 %
Nominal fracture strain	Nominal fracture strain	ISO 527-22	>50 %
Tensile strain	Tensile strain Yield	ISO 527-22	6.0 %
Tensile strain	Tensile strain	Tensile strain Yield	ISO 527-2/50	6.0 %
tensile strength	tensile strength Break	ISO 527-2/50	71.0 MPa
	tensile strength	tensile strength Yield	ISO 527-22	60.0 MPa
	tensile strength	tensile strength	tensile strength Yield	ISO 527-2/50	60.0 MPa
Tensile modulus	Tensile modulus	ISO 527-22	2300 MPa
Tensile modulus	Tensile modulus	Tensile modulus	ISO 527-2/50	2300 MPa
Bending modulus	Bending modulus	ISO 178	2400 MPa
bending strength	bending strength	ISO 178	97.0 MPa

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion MD	ISO 11359-22	7E-05 cm/cm/°C
Hot deformation temperature	Hot deformation temperature 0.45MPa,Annealed	ISO 75-2/B	144 °C
	Hot deformation temperature	Hot deformation temperature 0.45MPa	ISO 75-22	145 °C
		Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed	ISO 75-2/A	125 °C
			Hot deformation temperature	Hot deformation temperature 1.8MPa,Annealed	ISO 75-2/A	141 °C
			Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 1.8MPa	ISO 75-22	131 °C
Vicat softening temperature	Vicat softening temperature	ISO 306/B50	149 °C
Vicat softening temperature	Vicat softening temperature	Vicat softening temperature 50N	ISO 3062	149 °C
Ball pressure temperature	Ball pressure temperature	IEC 60335-1	125 °C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Shrinkage rate	Shrinkage rate MD	ISO 294-4	0.50to0.70 %
Melt Volume Flow Rate (MVR)	Melt Volume Flow Rate (MVR) 300°C/1.2kg	ISO 11332	8.00 cm³/10min
melt mass-flow rate	melt mass-flow rate 300°C/1.2kg	ISO 1133	10 g/10min
density	density	ISO 11832	1200 kg/m³
density	density	density	ISO 1183/A	1.20 g/cm³

Electrical performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Compared to the anti leakage trace index	Compared to the anti leakage trace index 2.00mm	IEC 60112	PLC 2
Dissipation factor	Dissipation factor 1MHz	IEC 602502	2E-03
Dissipation factor	Dissipation factor	Dissipation factor 100Hz	IEC 602502	1E-03
Relative permittivity	Relative permittivity 1MHz	IEC 602502	3.00
Relative permittivity	Relative permittivity	Relative permittivity 100Hz	IEC 602502	3.00
Dielectric strength	Dielectric strength	IEC 60243-12	17 kV/mm
Volume resistivity	Volume resistivity	IEC 600932	>1.0E+13 ohms·m

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.