mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Tensile modulus	Tensile modulus	ISO 527-2/1	2500 Mpa
tensile strength	tensile strength Yield2	ASTM D638	62.0 Mpa
	tensile strength	tensile strength Yield	ISO 527-2/50	57.0 Mpa
	tensile strength	tensile strength	tensile strength Break	ISO 527-2/50	50.0 Mpa
Tensile strain	Tensile strain Yield	ISO 527-2/50	4.5 %
	Tensile strain	Tensile strain Break2	ASTM D638	25 %
	Tensile strain	Tensile strain	Tensile strain Break	ISO 527-2/50	130 %
Bending modulus	Bending modulus 50.0 mm Span3	ASTM D790	2510 Mpa
Bending modulus	Bending modulus	Bending modulus --4	ISO 178	2500 Mpa
bending strength	bending strength --4,5	ISO 178	75.0 Mpa
bending strength	bending strength	bending strength Yield, 50.0 mm Span3	ASTM D790	88.0 Mpa

injection	Điều kiện kiểm tra	Kết quả kiểm tra
drying temperature	drying temperature	95 to 105 °C
drying time	drying time	3.0 to 4.0 hr
Suggested maximum moisture content	Suggested maximum moisture content	0.040 %
Suggested injection volume	Suggested injection volume	40 to 80 %
Temperature at the rear of the barrel	Temperature at the rear of the barrel	240 to 255 °C
Temperature in the middle of the barrel	Temperature in the middle of the barrel	245 to 260 °C
Temperature at the front of the material cylinder	Temperature at the front of the material cylinder	250 to 265 °C
Spray nozzle temperature	Spray nozzle temperature	245 to 265 °C
Processing (melt) temperature	Processing (melt) temperature	260 to 275 °C
Mold temperature	Mold temperature	55 to 70 °C
Back pressure	Back pressure	0.300 to 1.00 Mpa
Screw speed	Screw speed	30 to 80 rpm
Exhaust hole depth	Exhaust hole depth	0.038 to 0.076 mm

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Hot deformation temperature	Hot deformation temperature 0.45 MPa, Unannealed, 3.20 mm	ASTM D648	115 °C
	Hot deformation temperature	Hot deformation temperature 0.45 MPa, Unannealed, 4.00 mm, 64.0 mm Span7	ISO 75-2/Bf	116 °C
		Hot deformation temperature	Hot deformation temperature 1.8 MPa, Unannealed, 6.40 mm	ASTM D648	104 °C
		Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span7	ISO 75-2/Af	98.0 °C
Vicat softening temperature	Vicat softening temperature	ISO 306/B50	113 °C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion Flow : -20 to 150°C	ASTM E831	7.2E-5 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion Across Flow : -20 to 150°C	ASTM E831	7.2E-5 cm/cm/°C
thermal conductivity	thermal conductivity	ASTM C177	0.25 W/m/K

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
melt mass-flow rate	melt mass-flow rate 220°C/10.0 kg	ASTM D1238	5.0 g/10 min
	melt mass-flow rate	melt mass-flow rate 260°C/5.0 kg	ASTM D1238	14 g/10 min
	melt mass-flow rate	melt mass-flow rate	melt mass-flow rate 280°C/3.8 kg	ASTM D1238	24 g/10 min
Shrinkage rate	Shrinkage rate Flow : 3.20 mm	Internal Method	0.50 - 0.70 %
Shrinkage rate	Shrinkage rate	Shrinkage rate Across FlowFlow : 3.20 mm	Internal Method	0.50 - 0.70 %
Water absorption rate	Water absorption rate 24 hr	ASTM D570	0.25 %
Outdoor applicability	Outdoor applicability	UL 746C	f2

hardness	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Rockwell hardness	Rockwell hardness R-Scale	ASTM D785	110

hardness

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Rockwell hardness

R-Scale

ASTM D785

110

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.