PC+PET POCAN® C 1206 000000 LANXESS GERMANY

So sánh

Bảng thông số kỹ thuật

impact performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength 23°C	ISO 180/1U	NoBreak
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength -30°C	ISO 180/1U	NoBreak
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C	ISO 180/1A	50 kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap -30°C	ISO 180/1A	15 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength -30°C	ISO 179/1eA	20 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	Charpy Notched Impact Strength 23°C	ISO 179/1eA	55 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch -30°C	ISO 179/1eU	NoBreak
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch 23°C	ISO 179/1eU	NoBreak

mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
bending strength	bending strength 3.5%Strain	ISO 178/A	65.0 MPa
bending strength	bending strength	bending strength 23°C	ISO 178	75.0 MPa
Bending modulus	Bending modulus 23°C	ISO 178/A	2200 MPa
Nominal tensile fracture strain	Nominal tensile fracture strain 23°C	ISO 527-2/50	10 %
Tensile strain	Tensile strain Yield,23°C	ISO 527-2/50	4.5 %
tensile strength	tensile strength Yield,23°C	ISO 527-2/50	50.0 MPa
Tensile modulus	Tensile modulus 23°C	ISO 527-2/1	2200 MPa
bending strength	bending strength FlexuralStrainatFlexuralStrength5(23°C)		5.0 %

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion TD：23to55°C	ISO 11359-2	8E-05 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion MD：23to55°C	ISO 11359-2	9E-05 cm/cm/°C
Melting temperature	Melting temperature	ISO 11357-3	250 °C
Vicat softening temperature	Vicat softening temperature	ISO 306/B120	130 °C
Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed	ISO 75-2/A	90.0 °C
Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 0.45MPa,Unannealed	ISO 75-2/B	120 °C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Shrinkage rate	Shrinkage rate MD:120°C,2hr,2.00mm3	ISO 294-4	0.30 %
	Shrinkage rate	Shrinkage rate MD:270°C,2.00mm2	ISO 294-4	0.70 %
		Shrinkage rate	Shrinkage rate TD:120°C,2hr,2.00mm3	ISO 294-4	0.30 %
		Shrinkage rate	Shrinkage rate	Shrinkage rate TD:270°C,2.00mm2	ISO 294-4	0.70 %
Melt Volume Flow Rate (MVR)	Melt Volume Flow Rate (MVR) 260°C/5.0kg	ISO 1133	30.0 cm³/10min
Apparent density	Apparent density	ISO 60	0.80 g/cm³
density	density 23°C	ISO 1183	1.22 g/cm³

Supplementary Information	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
ISO Shortcut	ISO Shortcut	ISO 7792	PET+PC,GHMPR,09-020

Supplementary Information

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

ISO Shortcut

ISO 7792

PET+PC,GHMPR,09-020

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.