PP TechnoFin PP GF 20 TECHNOCOMPOUND GERMANY

So sánh

Bảng thông số kỹ thuật

impact performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch 23°C	ISO 179/1eU	30 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch -30°C	ISO 179/1eU	25 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength 23°C	ISO 179/1eA	5.0 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	Charpy Notched Impact Strength -30°C	ISO 179/1eA	4.1 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch -30°C	ISO 179/1eU	25 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch 23°C	ISO 179/1eU	30 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength -30°C	ISO 179/1eA	4.1 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	Charpy Notched Impact Strength 23°C	ISO 179/1eA	5.0 kJ/m²

mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
tensile strength	tensile strength Yield	ISO 527-2/50	45.0 MPa
tensile strength	tensile strength	tensile strength Break	ISO 527-2/5	55.0 MPa
Tensile strain	Tensile strain Yield	ISO 527-2/50	3.0 %
Tensile modulus	Tensile modulus	ISO 527-2/1	3500 MPa
bending strength	bending strength	ISO 178	84.9 MPa
Bending modulus	Bending modulus	ISO 178	4010 MPa
Tensile strain	Tensile strain Break	ISO 527-2/5	3.4 %
Tensile strain	Tensile strain	Tensile strain Yield	ISO 527-2/50	3.0 %
tensile strength	tensile strength Break	ISO 527-2/5	55.0 MPa
tensile strength	tensile strength	tensile strength Yield	ISO 527-2/50	45.0 MPa
Tensile modulus	Tensile modulus	ISO 527-2/1	3500 MPa
Tensile strain	Tensile strain Break	ISO 527-2/5	3.4 %
Bending modulus	Bending modulus	ISO 178	4010 MPa
bending strength	bending strength	ISO 178	84.9 MPa

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Hot deformation temperature	Hot deformation temperature 0.45MPa,Unannealed	ISO 75-2/B	155 °C
	Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed	ISO 75-2/A	119 °C
		Hot deformation temperature	Hot deformation temperature 0.45MPa,Unannealed	ISO 75-2/B	155 °C
		Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed	ISO 75-2/A	119 °C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Melt Volume Flow Rate (MVR)	Melt Volume Flow Rate (MVR) 230°C/2.16kg	ISO 1133	14.0 cm³/10min
density	density	ISO 1183	1.03 g/cm³
Melt Volume Flow Rate (MVR)	Melt Volume Flow Rate (MVR) 230°C/2.16kg	ISO 1133	14.0 cm³/10min
density	density	ISO 1183	1.03 g/cm³

Electrical performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Surface resistivity	Surface resistivity	IEC 60093	1E+13 ohms
Surface resistivity	Surface resistivity	IEC 60093	1E+13 ohms

Electrical performance

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Surface resistivity

IEC 60093

1E+13 ohms

Surface resistivity

IEC 60093

1E+13 ohms

hardness	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Ball Pressure Test	Ball Pressure Test	ISO 2039-1	59.0 MPa
Ball Pressure Test	Ball Pressure Test	ISO 2039-1	59.0 MPa

hardness

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Ball Pressure Test

ISO 2039-1

59.0 MPa

Ball Pressure Test

ISO 2039-1

59.0 MPa

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.