PC/ABS TAROBLEND 65 X0 Taro Plast S.p.A.

So sánh

Bảng thông số kỹ thuật

impact performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch 23°C	ISO 179/1eU	无断裂
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C	ASTM D256	450 J/m
Charpy Notched Impact Strength	Charpy Notched Impact Strength 23°C	ISO 179/1eA	20 kJ/m²

impact performance

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Impact strength of simply supported beam without notch

23°C

ISO 179/1eU

无断裂

Impact strength of cantilever beam gap

23°C

ASTM D256

450 J/m

Charpy Notched Impact Strength

23°C

ISO 179/1eA

20 kJ/m²

flammability	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
UL flame retardant rating	UL flame retardant rating 1.70mm	UL 94	V-0
Burning wire flammability index	Burning wire flammability index 2.00mm	IEC 60695-2-12	960 °C
Hot filament ignition temperature	Hot filament ignition temperature 1.60mm	IEC 60695-2-13	775 °C
Extreme Oxygen Index	Extreme Oxygen Index	ASTM D2863	32 %

mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
bending strength	bending strength	ISO 178	85.0 MPa
Tensile modulus	Tensile modulus	ISO 527-2/1	2500 MPa
tensile strength	tensile strength Yield	ISO 527-2/50	65.0 MPa
tensile strength	tensile strength	tensile strength Break	ISO 527-2/50	50.0 MPa
Tensile strain	Tensile strain Break	ISO 527-2/50	45 %
Bending modulus	Bending modulus	ISO 178	2450 MPa

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed	ISO 75-2/A	110 °C
Continuous use temperature	Continuous use temperature	IEC 60216	60.0 °C
Ball Pressure Test	Ball Pressure Test 125°C	IEC 60695-10-2	Pass
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion MD：-30to30°C	ISO 11359-2	7E-05 cm/cm/°C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Shrinkage rate	Shrinkage rate TD	Internal Method	0.40to0.74 %
Shrinkage rate	Shrinkage rate	Shrinkage rate MD	Internal Method	0.40to0.70 %
Water absorption rate	Water absorption rate 23°C,24hr	ISO 62	0.20 %
Water absorption rate	Water absorption rate	Water absorption rate Saturation,23°C	ISO 62	0.60 %
density	density	ISO 1183	1.18to1.20 g/cm³

Electrical performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Volume resistivity	Volume resistivity	IEC 60093	>1.0E+15 ohms·cm
Compared to the anti leakage trace index	Compared to the anti leakage trace index SolutionA	IEC 60112	PLC 3
Dielectric strength	Dielectric strength 2.00mm	IEC 60243-1	22 kV/mm

Electrical performance

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Volume resistivity

IEC 60093

>1.0E+15 ohms·cm

Compared to the anti leakage trace index

SolutionA

IEC 60112

PLC 3

Dielectric strength

2.00mm

IEC 60243-1

22 kV/mm

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.